Bonding element, bonding matrix and composite material having the bonding element, and method of manufacturing thereof

ABSTRACT

A bonding element, a bonding element matrix and composite materials with a wide range of attractive properties that may be optimized, including, but not limited to, mechanical properties, thermal properties, magnetic properties, optical properties and nuclear properties, as a result of a first layer and second layer structure or core, first layer, and second layer structure of the bonding elements, as well as methods for making the bonding elements and the corresponding ceramic and/or composite materials.

This application claims priority to U.S. Provisional Application Ser. No. 61/449,659, filed on Mar. 5, 2011, which is incorporated herein by reference.

FIELD OF INVENTION

The present invention generally relates to ceramic and/or composite materials. More specifically, the present invention relates to ceramic and/or composite materials that comprise bonding elements that improve mechanical and other properties associated with the ceramic and/or composite materials, as well as methods for making the bonding elements and the corresponding ceramic and/or composite materials.

BACKGROUND

Conventional ceramic materials, such as cement, concrete and other like materials can exhibit weak material properties. These weak material properties may be due to the fact that the bonds, for example hydrate bonds, in the material are often weak. Hydrate bonds are bonds that contain water in its molecular form. Hydrated Portland Cement is an example of a material that contains hydrate bonds such as CaO.2SiO₂.4H₂O and CaO.H₂O. This weakness may cause the ceramic material to be fail prematurely, which is clearly an undesirable material characteristic.

Thus, a need exists to improve the bonds and, more generally, the bonding matrix associated with ceramic materials, such as cement, concrete and other like materials, so as to provide ceramic materials with improved material properties.

All references cited herein in this specification are incorporated by reference in their entirety.

SUMMARY OF THE INVENTION

In accordance with exemplary embodiments of the present invention, the bonding elements, bonding matrixes, composite materials, and methods of making said bonding elements result a wide range of attractive properties that may be optimized, including, but not limited to, mechanical properties, thermal properties, magnetic properties, optical properties and nuclear properties, as a result of the core/first layer/second layer structure of the bonding elements.

Additional features and advantages of the invention will be set forth in the description which follows, and in part will be apparent from the description, or may be learned by practice of the invention. The objectives and other advantages of the invention will be realized and attained by the structure particularly pointed out in the written description and claims hereof as well as the appended drawings.

It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the Office upon request and payment of the necessary fee.

The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the principles of the invention. In the drawings:

FIGS. 1(a)-1(c) are schematic cross-sections of single bonding elements according to exemplary embodiments of the present invention, illustrating three exemplary core morphologies: FIG. 1(a)—fibrous, FIG. 1(b)—elliptical, and FIG. 1(c)—equiaxed.

FIGS. 2(a)-2(f) are side view and cross section views of composite materials according to exemplary embodiments of the present invention, illustrating: FIG. 2(a)—1D oriented fiber-shaped bonding elements in a dilute bonding matrix (bonding elements are not touching), FIG. 2(b)—2D oriented platelet shaped bonding elements in a dilute bonding matrix (bonding elements are not touching), FIG. 2(c)—3D oriented platelet shaped bonding elements in a dilute bonding matrix (bonding elements are not touching), FIG. 2(d)—randomly oriented platelet shaped bonding elements in a dilute bonding matrix (bonding elements are not touching), wherein the composite materials includes the bonding matrix and filler components such as polymers, metals, inorganic particles, aggregates etc., FIG. 2(e)—a concentrated bonding matrix (with a volume fraction sufficient to establish a percolation network) of bonding elements where the matrix is 3D oriented, and FIG. 2(f)—a concentrated bonding matrix (with a volume fraction sufficient to establish a percolation network) of randomly oriented bonding elements, wherein filler components such as polymers, metals, inorganic particles, aggregates etc. may be included. Structures comprising a mixture of bonding elements that touch one another and others that are dispersed units are also envisioned but not shown here. The bonding elements can comprise any of the basic multilayered structures shown in FIGS. 1(a)-1(c) or may have any additional morphologies, but are shown in an abbreviated form for this figure. Cross-sections of representative core particle morphologies are shown for clarity.

FIG. 3 illustrates different connectivity patterns in two component composite materials systems according to exemplary embodiments of the present invention. Shaded regions show the regions of bonding matrix, and non-shaded regions are filler components, such as metals, aggregates, inorganic particles or polymers. (FIG. 3 adapted from: R. E. Newnham, D. P. Skinner and L. E. Cross, “Connectivity and piezoelectric-pyroelectric composites”, Mat. Res. Bull. Vol. 13, pp. 525-536, 1978).

FIG. 4(a) shows a 3-0 composite material according to exemplary embodiments of the present invention, comprising a bonding matrix and equiaxed filler particles randomly distributed in the bonding matrix, and FIG. 4(b) shows a 3-1 composite material according to exemplary embodiments of the present invention comprising bonding matrix and oriented fiber-shaped filler components.

FIG. 5(a) shows a secondary electron (SE) and FIG. 5(b) shows a back scattered electron (BSE) scanning electron microscopy (SEM) images of a bonding matrix according to an exemplary embodiment of the present invention, composed of crystalline wollastonite core fibers encapsulated by amorphous silica and surrounded by CaCO₃ particles.

FIGS. 6(a)-6(c) show energy-dispersive X-ray spectroscopy (EDS) chemical mapping of a bonding matrix according to an exemplary embodiment of the present invention, illustrating superposition of Si (FIG. 6(a)) and Ca (FIG. 6(b)) map. In FIG. 6(c) the regions of CaSiO, SiO₂, and CaCO₃ are referenced by arrows. Fiber shaped wollastonite (CaSiO₃) core particles are encapsulated by SiO₂ rich regions and surrounded by CaCO₃ particles.

FIG. 7 shows a field emission scanning electron microscopy (FESEM) image of a Vicker's hardness indentation of 20 N on a P3 bonding matrix (Table 6) according to an embodiment of the present invention.

FIGS. 8(a)-8(c) show FESEM micrographs of: FIG. 8(a)—an indentation (SE Image), FIG. 8(b)—higher magnification of point marked D (BSE Image), and FIG. 8(c)—a robust interface between the core wollastonite grain and silica phase coating.

FIG. 9 shows a stress versus displacement curve of a P3 bonding matrix (also see Table 4) in compression of an embodiment of the present invention.

FIG. 10 shows a stress versus displacement curve of a FB4 composite material (see Table 3) in compression according to an exemplary embodiment of the present invention.

FIGS. 11(a)-11(d) show interaction of a P3 bonding matrix (also see Table 4) with FIG. 11(a)—SiO₂, FIG. 11(b)—SiO₂, FIG. 11(c)—high Ca Fly Ash (HCFA) and FIG. 11(d)—CaCO₃ according to embodiments of the present invention. Observation of the P3 bonding matrix and SiO₂ interface (FIGS. 11(a) and (b)) reveals that CaCO₃ particles and silica rich coating around wollastonite core fibers have formed an interface with externally added silica particles.

FIGS. 12(a)-12(b) illustrate the failure behavior of a 0-3 composite material according to an embodiment of the present invention. FIG. 12(a) shows the 0-3 composite, where 70 vol. % sand (silica) particulate components are dispersed in P3 bonding matrix with porosities in the structure (also see Table 4). As shown in FIG. 12(b), this composite material showed a gradual failure during compression, and had a compressive strength of ≈55 MPa.

FIGS. 13(a)-13(d) illustrate exemplary embodiments of the present invention having different levels of repeating hierarchic structures. FIGS. 13(a)-13(b) illustrate a 1-level hierarchic system with FIG. 13(b) illustrating a bonding matrix coating on coarse particles, and FIGS. 13(c)-13(d) illustrate a 2-level hierarchic system with FIG. 13(d) illustrating a bonding matrix coating on coarser particles.

FIGS. 14(a)-(c) show different optical micrographs of a composite material of Hydrate Free Concrete (HFC) according to an embodiment of the present invention. FIGS. 14(a) and 14(b) show optical micrographs at low (FIG. 14(a)) and higher (FIG. 14(b)) magnification of the composite material formed by using a volumetric ratio of 1:2:2 of FB1 Fiber Cores (Table 3), (300-500) μm sand, and (2-4) mm sand gravel respectively, and FIG. 14 (c) shows an SE FESEM micrograph of the bonding matrix dispersed around sand particle components, specifically in the void spaces of sand particles, and a thick layer of bonding matrix has surrounded sand particles to act as a cementing phase also.

FIGS. 15(a)-15(b) show microstrain versus temperature (FIG. 15(a)), and temperature versus time profile of FB1B during thermal cycling between −40° C. and 100° C. (FIG. 15(b)).

FIG. 16 shows a plot of specific heat (c_(p)) of P3 (Table 4) as a function of temperature. Experiment performed according to ASTM E1269.

FIGS. 17(a)-17(c) show digital photographs of, FIG. 17(a)—conventional natural sandstone and a sandstone mimic according to an embodiment of the present invention, FIG. 17(b)—conventional granite and a granite mimic according to an embodiment of the present invention, and FIG. 17(c)—conventional terracotta and a terracotta mimic according to an embodiment of the present invention.

FIG. 18 shows the effect of reaction time on compressive, and tensile strength of the bonding matrix (104° C. and ≈300 psi CO₂ initial starting pressure). P3 Bonding matrix is formed after 20 h reaction (Table 4).

FIGS. 19(a)-19(c) show plots of flexural strength versus displacement of FB1B bonding matrix with metal fibers according to an embodiment of the present invention (FIG. 19(a)), pristine CPC2 matrix (Curve A) according to an embodiment of the present invention, and CPC2 with 10 wt % metal fibers (curve C, composition FRCPC2, Table 16) and with 2.5 wt % PVA fibers (Curve B) according to embodiments of the present invention (FIG. 19(b)), and comparison of the flexural strength of FB1B bonding matrix with 10 wt % as received and oxidized (rusted) metal fibers (compositions FRCPC2 and RFRCPC2, Table 16) (FIG. 19(c)).

FIGS. 20(a)-(f) show SE (FIG. 20(a)) and BSE images (FIG. 20(b)) of interface of steel fibers a bonding matrix according to an embodiment of the present invention, and EDS chemical mapping of Ca (FIG. 20(c)), Si (FIG. 20(d)), Fe (FIG. 20(e)), and O (FIG. 20(f)).

FIG. 21 shows SE FESEM microstructure of SRC3 composite material (also see Table 18) according to an embodiment of the present invention.

FIG. 22 shows a plot of flexural stress versus displacement of a FSRBC1 composite material (also see Table 19), and a digital photograph, showing bending of the FSRBC1 composite material during testing in an INSTRON system.

FIGS. 23(a)-(c) show FESEM, SE (FIG. 23(a)) and BSE (FIG. 23(b)) images of the microstructure of carbonated olivine according to an embodiment of the present invention, and at higher magnifications, BSE (FIG. 23(c)), SE (FIG. 23(d)), and BSE (FIG. 23(e))_images of carbonated olivine particles of different morphologies.

FIGS. 24(a)-24(d) show FESEM, SE (FIG. 24(a)) and BSE (FIG. 24(b)) images of the microstructure of carbonated diopside according to an embodiment of the present invention, and at higher magnifications, and SE (FIG. 24(c)) and, BSE (FIG. 24(d)) images of carbonated diopside particles.

FIG. 25 shows the polyhedrons presented in Table 1.

DETAILED DESCRIPTION OF THE ILLUSTRATED EMBODIMENTS

Reference will now be made in detail to an embodiment of the present invention, example of which is illustrated in the accompanying drawings.

Bonding Element

FIGS. 1(a)-1(c) illustrate the cross-section of exemplary bonding elements that may make up at least a portion of a larger ceramic or composite material. As shown in FIGS. 1(a)-1(c), a given bonding element includes a core, represented by the black inner portion; a first layer, represented by the white middle portion; and a second or encapsulating layer, represented by the outer portion.

In accordance with exemplary embodiments of the present invention, a bonding element may exhibit any size and morphology (i.e., shape) depending on the intended application. Table 1 provides a non-exclusive list of possible morphologies. The first layer may include only one layer or multiple sub-layers depending on the chemistry of the bonding element and may completely cover the core or partially cover the core. The first layer may exist in a crystalline phase, an amorphous phase or a combination thereof. The second layer may include only one layer or multiple sub-layers and may also completely or partially cover the first layer. The second layer may also comprise a plurality of particles or may be of a continuous phase, with minimal observable discrete particles.

TABLE 1 Regular Geometries (Symmetrical Solids) Polyhedrons are solid made of flat surfaces. Each surface is a polygon. E.g. Platonic solids, Prisms, Pyramids Non-polyhedrons are solids having a curved surfaces or mix of curved and flat surfaces. E.g. Sphere, Torus, Cylinder, Cone. Name Description Cube A cube is a three dimensional solid with 6 matching square sides. Particle shape having equal length, breadth and thickness, with angles of 90°, and smooth surfaces Rectangular In a rectangular solid, the length, width and height may be of different Solids, Cuboids lengths Prism A prism is a solid that has two congruent parallel bases that are polygons. The polygons form the bases of the prism and the length of the edge joining the two is called the height. Disc Particle with an approximately circular cross section, the diameter of which is large in comparison to thickness (D:T = (1.3 − 10):1) Pyramid A pyramid is a solid with a polygon base and connected by triangular faces to its vertex. A pyramid is a regular pyramid if its base is a regular polygon and the triangular faces are all congruent isosceles triangles. Complex The following lists the name given to a polyhedron having n faces. polyhedrons OR n faces Name multifaceted  4 tetrahedron particles  5 pentahedron  6 hexahedron  7 heptahedron  8 octahedron  9 nonahedron 10 decahedron 11 undecahedron 12 dodecahedron 14 tetmdecahedron 20 icosahedron 24 icositetrahedron 30 triacontahedron 32 icosidodecahedron 60 hexecontahedron 90 enneacontahedron Cylinder A cylinder is a solid with two congruent circles joined by a curved surface. Round cross-section Sphere A sphere is a solid with all its points the same distance from the center. Particle of equal diameter in all directions, having infinite rotational symmetry and a smooth surface Cone A circular cone has a circular base, which is connected by a curved surface to its vertex. A cone is called a right circular cone, if the line from the vertex of the cone to the center of its base is perpendicular to the base. Pointed in conical fashion Hollow Structures: Geometrical Solids with a Cavity in the Center

Name Description Ring toroidal shape Tube long hollow object (usually cylindrical) Other Qualitative Powder Morphology Descriptors (Mostly for Irregular Solids)

Name Description Acicular needle-shaped slender, needle-shape for a particle of similar breadth and thickness, which are much smaller than length (L:B:T = (10- 100):~1:~1); Length (L), Breadth (B) and Thickness (T) Angular sharp-edged or having roughly polyhedral shape particle shape showing sharp edges or having approximately polyhedral shape Sharp edges, prominent, slightly rounded or straight or piecewise crooked but not wiggly Bent Overall form is curved Channels Relatively rounded grooves Concave Dish like or prominent pit or hollow Crescent Noodle, or at least quarter noon Columnar long, thin particle shape showing a breadth and thickness that are greater than those of an acicular particle (L:B:T = (3- 10):~1:~1) Dendritic Having a branched crystalline shape particle shape showing a typical pine tree structure (highly branched) Equant Length and width of outline roughly equal Euhedral All or nearly all faces are flat Fiber, Regular or irregularly thread-like Fibrous threadlike particle, which has a very large length/diameter ratio (longer and thinner than acicular particles) (L:B:T = (>100):~1:~1) (typical diameter about 0.1-10 mm) Flake, Flaky Plate-like thin, flat particle of similar length and breadth (L:B:T = ~1:~1:(<0.1)) (often with some curvature of surface, which will increase thickness) Very flat, sheet like, nearly 2 dimensional Flattened Oblate, thicker than flake, not bent Fractal Particle that shows self similarity at different size scales Glass like Smooth angular, or chonchoidal features Grape like Uniform and closely rounded bumps Granular Having approximately an equidimensional irregular shape particle shape that is irregular but has about equal dimensions larger than about 1 mm (L:B:T = ~1:~1:(0.5-2)) Irregular Lacking any symmetry Particle of about equal dimensions lacking any symmetry Layers Any evidence of parallel sheets, layers, cleavage Long-thin Length greater than width Lumpy Prominent protruding rounded bumps Lath long, thin and blade-like particle (L:B:T = (10-50):(2-5):1) Modular Having rounded, irregular shape Needle See acicular Oblong Length of outline greater than width Plate Flat particle of similar length and breadth but with greater thickness than flake (L:B:T = ~1:~1:(0.1-0.6)), but without surface curvature Potato Rounded, oblong, sub-smooth with dirt like decoration Ribbon Long, thin, and relatively flat Ripples Small or shallow roughly parallel waves of folds, unlike striations, which are more like scratches Rod Particle with a circular cross section, the diameter of which is smaller than length (L:DA = (2-5):1) Rounded Particle of any shape, usually having similar length, breadth and thickness, with rounded edges At least one surface is rounded, or most of the overall form looks rounded Shard Flattened, smooth broken edges Smoothed Looks smooth as if by melting or by a covering of glue Eraser Shape of a eraser Burrito Shape of a burrito Africa Shape of Africa Jelly Fish Shape of a Jell Fish Worm Shape of a worm Subhedral At least two prominent flat faces Striated Closely parallel scratches Subangular Rounded straight edges Subsphere Out of round but roughly spherical Twisted Appear wrung or twisted by end

A bonding element is produced through a transformation process. This process will be described in greater detail below. In general, however, the process involves the transformation of reactive precursor particles. The precursor particles may have any desired size and shape and may be similar in size and shape, or they may vary. The transformation of a given precursor particle will result in a corresponding bonding element having a similar size and shape. The transformation process proceeds by exposing the precursor particles to a reactive liquid. A reactant associated with the liquid then reacts with the chemical elements that make up the precursor particles, and more specifically, the chemical elements in the peripheral portion of the precursor particles. This reaction eventually results in the formation of the aforementioned first and second layers.

In a first embodiment of the above-described bonding element, the precursor particles comprise two or more chemical elements, such as a ceramic material comprising multiple cations or a metallic material comprising multiple metals. During the transformation process, the reactant in the liquid preferentially reacts with at least a first one of the chemical elements, wherein the reaction between the reactant and the at least one first chemical element results in the formation of the first and second layers, the first layer comprising a derivative of the precursor particle, generally excluding the at least one first chemical element, whereas the second layer comprises a combination of the reactant and the at least one first chemical element. In comparison, the core comprises the same or nearly the same chemical composition as the precursor particle. For example, peripheral portions of the core may vary from the chemical composition of the precursor particle due to selective leaching of particular chemical elements from the core.

Thus, the core and the second layer share the at least one first chemical element of the precursor particle, and the core and the first layer share at least another one of the chemical elements of the precursor particle. The at least one first chemical element shared by the core and the second layer may be, for example, at least one alkaline earth element (beryllium, magnesium, calcium, strontium, barium and radium). The at least another one of the chemical elements shared by the core and the first layer may be, for example, silicon, titanium, aluminum, phosphorus, vanadium, tungsten, molybdenum, gallium, manganese, zirconium, germanium, copper, niobium, cobalt, lead, iron, indium, arsenic and/or tantalum.

In a second exemplary embodiment, the precursor particles can still comprise two or more chemical elements; however, during the transformation process, the reactant in the liquid preferentially reacts with at least a first one of the chemical elements, wherein the reaction between the reactant and the at least one first chemical element results in the formation of the first and second layers, the first layer and second layer both comprising a combination of the reactant and the at least one first chemical element. Thus, the cations associated with the chemical composition of the first layer correspond to a first one of the two or more chemical elements of the precursor particles, and the cations associated with the second layer also correspond to the first one of the two or more chemical elements of the precursor particles.

In yet an alternative exemplary embodiment, the reaction between the reactant and the at least one first chemical element of the precursor particles may be carried out to completion thus resulting in the first layer becoming the core of the bonding element and having a chemical composition that is different from that of the precursor particles, and at least one additional or second shell layer comprising a composition that may or may not include the at least one first chemical element of the two or more chemical elements of the precursor particles.

The precursor particles can be selected from any suitable material that can undergo the above-describe transformation. For example, the precursor particles may include oxides and non-oxides of silicon, titanium, aluminum, phosphorus, vanadium, tungsten, molybdenum, gallium, manganese, zirconium, germanium, copper, niobium, cobalt, lead, iron, indium, arsenic, tantalum, and/or alkaline earth elements (beryllium, magnesium, calcium, strontium, barium and radium). For example, the precursor particle may include oxides such as silicates, titanates, aluminates, phosphates, vanadates, tungstates, molybdates, gallates, manganates, zirconates, germinates, cuprates, stannates, hafnates, chromates, niobates, cobaltates, plumbates, ferrites, indates, arsenates, tantalates and combinations thereof. In a preferred embodiment, the precursor particles include silicates such as orthosilicates, sorosilicates, cyclosilicates, inosilicates, phyllosilicates, tectosilicates and/or calcium silicate hydrate. It is believed that the various specific silicates listed in Table 2A may be used as the precursor particle. It is also believed that various specific non-silicates listed in Table 2A may be used as the precursor particle and that the various rock containing materials as listed in Table 2A can be used as the precursor particle.

TABLE 2A List of reactive precursors 1. Silicates Nesosilicates or Nesosilicates (from Phenacite group orthosilicates Greek νησoζ nēsos, Phenacite—Be2SiO4 island), or orthosilicates, Willemite—Zn₂SiO₄ have isolated (insular) Olivine group [SiO₄]⁴⁻tetrahedra that Forsterite—Mg₂SiO₄ are connected only by Fayalite—Fe₂SiO₄ interstitial cations. Garnet group Pyrope—Mg₃Al₂(SiO₄)₃ Almandine—Fe₃Al₂(SiO₄)₃ Spessartine—Mn₃Al₂(SiO₄)₃ Grossular—Ca₃Al₂(SiO₄)₃ Andradite—Ca₃Fe₂(SiO₄)₃ Uvarovite—Ca₃Cr₂(SiO₄)₃ Hydrogrossular—Ca₃Al₂Si₂O₈(SiO₄)_(3-m)(OH)_(4m) Zircon group Zircon—ZrSiO₄ Thorite—(Th,U)SiO₄ Kyanite crystals Al₂SiO₅ group Andalusite—Al₂SiO₅ Kyanite—Al₂SiO₅ Sillimanite—Al₂SiO₅ Dumortierite—Al_(6.5-7)BO₃(SiO₄)₃(O,OH)₃ Topaz—Al₂SiO₄(F,OH)₂ Staurolite—Fe₂Al₉(SiO₄)₄(O,OH)₂ Humite group—(Mg,Fe)₇(SiO₄)₃(F,OH)₂ Norbergite—Mg₃(SiO₄)(F,OH)₂ Chondrodite—Mg₅(SiO₄)(F,OH)₂ Humite—Mg₇(SiO₄)(F,OH)₂ Clinohumite—Mg₉(SiO₄)(F,OH)₂ Datolite—CaBSiO₄(OH) Titanite—CaTiSiO₅ Chloritoid—(Fe,Mg,Mn)₂Al₄Si₂O₁₀ (OH) Sorosilicates Sorosilicates have Hemimorphite (calamine)—Zn₄(Si₂O₇)(OH)₂•H₂O isolated double Lawsonite—CaAl₂(Si₂O₇)(OH)₂•H₂O tetrahedra groups with Ilvaite—CaFe²⁺ ₂Fe³⁺O(Si₂O₇)(OH) (Si₂O₇)⁶⁻ or a ratio of Epidote group (has both (SiO₄)⁴⁻ and (Si₂O₇)⁶⁻ groups) 2:7. Epidote—Ca₂(Al,Fe)₃O(SiO₄)(Si₂O₇)(OH) Zoisite—Ca₂Al₃O(SiO₄)(Si₂O₇)(OH) Clinozoisite—Ca₂Al₃O(SiO₄)(Si₂O₇)(OH) Tanzanite—Ca₂Al₃O(SiO₄)(Si₂O₇)(OH) Allanite—Ca(Ce,La,Y,Ca)Al₂(Fe²⁺,Fe³⁺)O(SiO₄)(Si₂O₇)(OH) Dollaseite-(Ce)—CaCeMg₂AlSi₃O₁₁F(OH) Vesuvianite (idocrase)—Ca₁₀(Mg,Fe)₂Al₄(SiO₄)₅(Si₂O₇)₂(OH)₄ Cyclosilicates Cyclosilicates, or ring 3-member ring silicates, have linked Benitoite—BaTi(Si₃O₉) tetrahedra with 4-member ring (Si_(x)O_(3x))^(2x−) or a ratio of Axinite—(Ca,Fe,Mn)₃Al₂(BO₃)(Si₄O₁₂)(OH) 1:3. These exist as 3− 6-member ring member (Si₃O₉)⁶⁻, 4− Beryl/Emerald—Be₃Al₂(Si₆O₁₈) member (Si₄O₁₂)⁸⁻ and Cordierite—(Mg,Fe)₂Al₃(Si₅AlO₁₈) 6−member (Si₆O₁₈)¹²⁻ Tourmaline—(Na,Ca)(Al,Li,Mg)³⁻(Al,Fe,Mn)₆(Si₆O₁₈)(BO₃)₃(OH)₄ rings. Inosilicates Inosilicates (from Greek ιζ [genitive: ινoζ], fibre), or chain silicates, have interlocking chains of silicate tetrahedra with either SiO₃, 1:3 ratio, for single chains or Si₄O₁₁, 4:11 ratio, for double chains. Single chain Pyroxene group inosilicates Enstatite—orthoferrosilite series Enstatite—MgSiO₃ Ferrosilite—FeSiO₃ Pigeonite—Ca_(0.25)(Mg,Fe)_(1.75)Si₂O₆ Diopside—hedenbergite series Diopside—CaMgSi₂O₆ Hedenbergite—CaFeSi₂O₆ Augite—(Ca,Na)(Mg,Fe,Al)(Si,Al)₂O₆ Sodium pyroxene series Jadeite—NaAlSi₂O₆ Aegirine (Acmite)—NaFe³⁺Si₂O₆ Spodumene—LiAlSi₂O₆ Pyroxenoid group Wollastonite—CaSiO₃ Rhodonite—MnSiO₃ Pectolite—NaCa₂(Si₃O₈)(OH) Double chain Amphibole group inosilicates Anthophyllite—(Mg,Fe)₇Si₈O₂₂(OH)₂ Cumingtonite series Cummingtonite—Fe₂Mg₅Si₈O₂₂(OH)₂ Grunerite—Fe₇Si₈O₂₂(OH)₂ Tremolite series Tremolite—Ca₂Mg₅Si₈O₂₂(OH)₂ Actinolite—Ca₂(Mg,Fe)₅Si₈O₂₂(OH)₂ Hornblende—(Ca,Na)²⁻³(Mg,Fe,Al)₅Si₆(Al,Si)₂O₂₂(OH)₂ Sodium amphibole group Glaucophane—Na₂Mg₃Al₂Si₈O₂₂(OH)₂ Riebeckite ( )—Na₂Fe²⁺ ₃Fe³⁺ ₂Si₈O₂₂(OH)₂ Arfvedsonite—Na₃(Fe,Mg)₄FeSi₈O₂₂(OH)₂ Phyllosilicates Phyllosilicates (from Greek φ{umlaut over (υ)}λλoν phyllon, leaf), or sheet silicates, form parallel sheets of silicate tetrahedra with Si₂O₅ or a 2:5 ratio. Kaolin Serpentine group Antigorite—Mg₃Si₂O₅(OH)₄ Chrysotile—Mg₃Si₂O₅(OH)₄ Lizardite—Mg₃Si₂O₅(OH)₄ Clay mineral group Halloysite—Al₂Si₂O₅(OH)₄ Kaolinite—Al₂Si₂O₅(OH)₄ Illite—(K,H₃O)(Al,Mg,Fe)₂(Si,Al)₄O₁₀[(OH)₂,(H₂O)] Montmorillonite—(Na,Ca)_(0.33)(Al,Mg)₂(Si₄O₁₀)(OH)₂•nH₂O Vermiculite—(MgFe,Al)₃(Al,Si)₄O₁₀(OH)₂•4H₂O Talc—Mg₃Si₄O₁₀(OH)₂ Palygorskite—(Mg,Al)₂Si₄O₁₀(OH)•4(H₂O) Pyrophyllite—Al₂Si₄O₁₀(OH)₂ Mica group Biotite—K(Mg,Fe)₃(AlSi₃O₁₀(OH)₂ Muscovite—KAl₂(AlSi₃O₁₀)(OH)₂ Phlogopite—KMg₃Si₄O₁₀(OH)₂ Lepidolite—K(Li,Al)2⁻³(AlSi₃O₁₀)(OH)₂ Margarite—CaAl₂(Al₂Si₂O₁₀)(OH)₂ Glauconite—(K,Na)(Al,Mg,Fe)₂(Si,Al)₄O₁₀(OH)₂ Chlorite group Chlorite—(Mg,Fe)₃(Si,Al)₄O₁₀(OH)₂•(Mg,Fe)₃(OH)₆ Tectosilicates Tectosilicates, or Feldspar group “framework silicates,” Alkali-feldspars have a three-dimensional Potassium-feldspars framework of silicate Microcline—KAlSi₃O₈ tetrahedra with SiO₂ or a Orthoclase—KAlSi₃O₈ 1:2 ratio. This group Sanidine—KAlSi₃O₈ comprises nearly 75% of Anorthoclase—(Na,K)AlSi₃O₈ the crust of the Earth. Plagioclase feldspars Tectosilicates, with the Albite—NaAlSi₃O₈ exception of the quartz Oligoclase—(Na,Ca)(Si,Al)₄O₈ (Na:Ca 4:1) group, are Andesine—(Na,Ca)(Si,Al)₄O₈ (Na:Ca 3:2) aluminosilicates. Labradorite—(Na,Ca)(Si,Al)₄O₈ (Na:Ca 2:3) Bytownite—(Na,Ca)(Si,Al)₄O₈ (Na:Ca 1:4) Anorthite—CaAl₂Si₂O₈ Feldspathoid group Nosean—Na₈Al₆Si₆O₂₄(SO₄) Cancrinite—Na₆Ca₂(CO₃,Al₆Si₆O₂₄)•2H₂O Leucite—KAlSi₂O₆ Nepheline—(Na,K)AlSiO₄ Sodalite—Na₈(AlSiO₄)₆Cl₂ Hauyne—(Na,Ca)⁴⁻⁸Al₆Si₆(O,S)₂₄(SO₄,Cl)₁₋₂ Lazurite—(Na,Ca)₈(AlSiO₄)₆(SO₄,S,Cl)₂ Petalite—LiAlSi₄O₁₀ Scapolite group Marialite—Na₄(AlSi₃O₈)₃(Cl₂,CO₃,SO₄ Meionite—Ca₄(Al₂Si₂O₈)₃(Cl₂CO₃,SO₄) Analcime—NaAlSi₂O₆•H₂O Zeolite group Natrolite - Na₂Al₂Si₃O₁₀•2H₂O Chabazite - CaAl₂Si₄O₁₂•6H₂O Heulandite - CaAl₂Si₇O₁₈•6H₂O Stilbite - NaCa₂Al₅Si₁₃O₃₆•17H₂O Calcium silicate hydrate: this is the main reaction product and is the main source of concrete strength. It is often abbreviated, using cement chemists' notation, to “C-S-H,” the dashes indicating that no strict ratio of SiO₂ to CaO is inferred. The Si/Ca ratio is somewhat variable but typically approximately 0.45-0.50.

It is also believed that some waste materials may be used as the precursor particles. Waste materials may include, for example, minerals, industrial waste, or an industrial chemical material. Some exemplary waste materials include mineral silicate, iron ore, periclase, gypsum, iron (II) hydroxide, fly ash, bottom ash, slag, glass, oil shells, red mud, battery waste, recycled concrete, mine tailings, paper ash, or salts from concentrated reverse osmosis brine.

Additional precursor particles may include different types of rock containing minerals such as cal-silicate rock, fitch formation, hebron gneiss, layered gneiss, middle member, argillite, quartzite, intermediate Precambrian sediments, dark-colored, feldpathic quartzite with minor limestone beds, high-grade metasedimentry biotite schist, biotite gniss, mica schist, quartzite, hoosac formation, partridge formation, Washington gneiss, Devonian, Silurian greenvale cove formation, ocoee supergroup, metasandstone, metagraywacke, Rangeley formation, amphibolites, calcitic and dolomite marble, manhattan formation, rusty and gray biotite-quartz-feldspar gneiss, and waterford group.

Precursor particles may also include igneous rocks such as, but not limited to, andesite, anorthosite, basinite, boninite, carbonatite and charnockite, sedimentary materials such as, but not limited to, argillite, arkose, breccias, cataclasite, chalk, claystone, chert, flint, gitsone, lighine, limestone, mudstone, sandstone, shale, and siltsone, metamorphic materials such as, but not limited to, amphibolites, epidiorite, gneiss, granulite, greenstone, hornfels, marble, pelite, phyllite, quartzite, shist, skarn, slate, talc carbonate, and soapstone, and other varieties of rocks such as, but not limited to, adamellite, appinite, aphanites, borolanite, blue granite, epidosite, felsites, flint, ganister, ijolite, jadeitite, jasproid, kenyte, vogesite, larvikite, litchfieldite, luxullianite, mangerite, minette, novaculite, pyrolite, rapakivi granite, rhomb porphyry, shonkinite, taconite, teschenite, theralite, and variolite.

Likewise, the first layer may comprise any chemical composition that may be derived from the chemical compositions of the various precursor materials described above.

As explained previously, the second, encapsulating layer, may comprise a combination of the reactant and the at least one chemical element from the precursor particle. In accordance with exemplary embodiments of the present invention, the second or encapsulating layer can comprise a number of possible chemistries. For examples, the encapsulating layer may comprise a carbonate having a naturally occurring structure. The second or encapsulating layer may also comprise other possible carbonate chemistries, as well as sulfates, phosphates and other anionic compounds capable of dissolving in a solvent and reacting with a precursor particle.

Table 2B provides exemplary embodiments of different types of chemistries for the first and second layers that can be achieved when using different precursor materials. The examples listed in Table 2B should not be viewed as limiting or as an exhaustive list of possible materials but only as exemplary as many different additional types of chemistries may be achieved depending on the precursor material. Regarding the first layer, by using different precursor materials one may obtain silica, alumina or titania. The second layer may also be modified with the selection of the precursor material. For example, the non-exhaustive list of materials for the second layer exemplified in Table 2B may include various types of carbonates such as, but not limited to, pure carbonates, multiple cations carbonates, carbonates with water or an OH group, layered carbonates with either water or an OH group, anion containing carbonates, silicate containing carbonates, and carbonate-bearing minerals.

TABLE 2B Concept showing how different raw materials (precursors) can be used to generate different types of encapsulating layers Raw Material (Precursor) from Table 2A First Layer Encapsulating Layer Type of Carbonate Wollastonite (CaSiO₃) Silica-rich CaCO₃ Pure carbonate Fosterite (Mg₂SiO₄) MgCO₃ Diopside (CaMgSi₂O₆) (Ca, Mg)CO₃ Multiple Cation carbonates Talc (Mg₃Si₄O₁₀(OH)₂) MgCO₃xH₂O (x = 1-5) Pure carbonate with H₂O Glaucophane Alumina MgCO₃ and/or Pure carbonate with OH (Na₂Mg₃Al₂Si₈O₂₂(OH)₂) and/or NaAlCO₃(OH)₂ group Palygorskite Silica-rich Mg₆Al₂CO₃(OH)₁₆4H₂O Layered carbonates with ((Mg,Al)₂Si₄O₁₀(OH)•4(H₂O)) OH and H₂O group Meionite (Ca₄(Al₂Si₂O₈)₃(Cl₂CO₃, SO₄)) Ca₂SO₄CO₃•4H₂O Anion-containing carbonates Tanzanite (Ca₂Al₃O(SiO₄)(Si₂O₇)(OH)) Ca₅Si₂O₈CO₃ and/or Silicate-containing carbonates Ca₅Si₂O₈CO₃ and/or Ca₇Si₆O₁₈CO₃•2H₂O (Ba_(0.6)Sr_(0.3)Ca_(0.1))TiO₃ Titania-rich Sr(Sr, Ca, Ba)(CO3)2 Post-1992 Carbonate-Bearing Minerals

To further provide additional guidance on how to achieve the above exemplary embodiments listed in Table 2B, the following is a more detailed discussion on how to achieve some of these exemplary materials.

Referring again to FIGS. 1(a)-1(c), three different, exemplary morphologies for the bonding elements are illustrated. The shape or morphology associated with the core and/or the bonding element may be the same or similar to the shape of the precursor particle. Thus, the precursor particle and, accordingly, the corresponding bonding element and/or core may take on any of a number of morphologies, including but not limited to a spherical shape, an elliptical shape, a polygonal shape, such as a hexagon, or any of a number of other shapes. Furthermore, the morphology of the precursor particle and, accordingly, the corresponding bonding element and/or core may be equiaxed or have one axis longer than another, as in the case of a wire or a rod shape. Still further, the precursor particle may comprise one crystal (i.e., “single crystalline”) or a plurality of crystals (i.e., “polycrystalline”). The precursor particle may actually comprise a plurality of particles or include an amorphous phase.

In a first specific example, a precursor particle formed predominately of wollastonite, CaSiO₃, reacts with carbon dioxide dissolved in water. It is believed that calcium cations are leached from the wollastonite and thereby change the peripheral portion of the wollastonite core into calcium-deficient wollastonite. As the calcium cations continue to be leached from the peripheral portion of the core, the structure of the peripheral portion eventually become unstable and breaks down, thereby transforming the calcium-deficient wollastonite peripheral portion of the core into a predominantly silica-rich first layer. Meanwhile, it is believed that a predominantly calcium carbonate second layer precipitates from the water. More specifically, the first layer and second layer may be formed from the precursor particle according the following reaction: H₂O+CaSiO₃+CO₂=CaCO₃+SiO₂+H₂O

The reactant of the reactive liquid, here carbon dioxide, preferentially reacts with the Ca cations of the wollastonite precursor core, thereby transforming the peripheral portion of the precursor core into a silica-rich first layer and a calcium carbonate-rich second layer. Also, the presence of the first and second layers on the core act as a barrier to further reaction between wollastonite and carbon dioxide, thus resulting in the bonding element having the core, first layer and second layer.

In this and other examples of the first embodiment, both the anions and cations vary in the respective layers. In this example, the core has Ca⁺², Si⁻⁴ and O²⁻ ions, the second layer has mostly Si⁺⁴ and O²⁻ and a small amount of Ca²⁺ ions, while the second layer has Ca²⁺ and CO₃ ²⁻ ions.

In a second example of the first embodiment, a precursor particle formed predominately of forsterite, Mg₂SiO₄, reacts with dissolved carbon dioxide transforming a peripheral portion of the forsterite into a predominantly silica first layer and a predominantly magnesium carbonate second layer. More specifically, the first layer and second layer may be formed from the precursor particle according the following reaction: H₂O+Mg_(x)Si_(y)O_(z)+CO₂ =xMgCO₃ +ySiO₂+H₂O

The reactant of the reactive liquid, here carbon dioxide, preferentially reacts with the Mg cations of the forsterite precursor core, thereby transforming the peripheral portion of the precursor particle into a silica-rich first layer and a magnesium carbonate rich second layer. Also, the presence of the first and second layers on the core act as a barrier to further reaction between forsterite and carbon dioxide, thus resulting in the bonding element having the core, first layer and second layer.

In a third example of the first embodiment, a precursor particle formed predominately of talc, Mg₃Si₄O₁₀(OH)₂, is preheated at 900° C. for 12 hours, to form dehydrated talc, reacts with dissolved carbon dioxide transforming a peripheral portion of the talc into a predominantly silica first layer and second layer formed predominantly of MgCO₃.xH₂O(x=1-5) More specifically, the first layer and second layer may be formed from the precursor particle according the following reaction: H₂O+Mg₃Si₄O₁₀(OH)₂+CO₂═MgCO₃ .xH₂O(x=1-5)+SiO₂+H₂O

The reactant of the reactive liquid, here carbon dioxide, preferentially reacts with the Mg cations of the talc, thereby transforming the peripheral portion of the precursor particle into a silica-rich first layer and a second layer rich with MgCO₃.xH₂O(x=1-5). Also, the presence of the first and second layers on the core act as a barrier to further reaction between talc and carbon dioxide, thus resulting in the bonding element having the core, first layer and second layer.

In a fourth example of the first embodiment, a precursor particle formed predominately of diopside, MgCaSi₂O₆, reacts with dissolved carbon dioxide transforming a peripheral portion of the diopside into a predominantly silica first layer and second layer formed predominantly of a mixture of calcium carbonate, CaCO₃, and magnesium carbonate, MgCO₃ and/or dolomite (Mg,Ca)CO₃ with variable ration of Mg and Ca. The second layer may include, for example, a first sub-layer of magnesium carbonate and a second sub-layer of calcium carbonate. Alternatively, the second layer may include a plurality of carbonated particles, such as CaCO₃ (Mg,Ca)CO₃ and MgCO₃.

The first layer and second layer may be formed from the precursor particle according to one or a combination of both the following reactions: H₂O+MgCaSi₂O₆+CO₂=MgCO₃+CaCO₃+SiO₂+H₂O H₂O+MgCaSi₂O₆+CO₂=2(Mg_(x),Ca_(y))CO₃+SiO₂+H₂O

The reactant of the reactive liquid, here carbon dioxide, preferentially reacts with the Ca and Mg cations of the diopside, thereby transforming the peripheral portion of the precursor particle into a silica-rich first layer and a second layer rich with a mixture of calcium carbonate and magnesium carbonate and/or dolomite with variable ratio of Mg and Ca. Also, the presence of the first and second layers on the core act as a barrier to further reaction between diopside and carbon dioxide, thus resulting in the bonding element having the core, first layer and second layer.

In a fifth example of the first embodiment, the precursor particle/core is be formed of glaucophane, Na₂Mg₃Al₂Si₈O₂₂(OH)₂, the first layer is alumina- and/or silica-rich, and the second layer is MgCO₃ and/or NaAlCO₃(OH)₂.

In a sixth example of the first embodiment, the precursor particle/core is formed of palygorskite, (Mg,Al)₂Si₄O₁₀(OH).4(H₂O), the first layer is alumina- and/or silica-rich, and the second layer is Mg₆Al₂CO₃(OH)₁₆.4H₂O.

In a seventh example of the first embodiment, the precursor particle/core is formed of meionite, Ca₄(Al₂Si₂O₈)₃(Cl₂CO₃,SO₄), the first layer is alumina- and/or silica-rich, and the second layer is Ca₂SO₄CO₃.4H₂O.

In an eighth example of the first embodiment, the precursor particle/core is formed of tanzanite, Ca₂Al₃O(SiO₄)(Si₂O₇)(OH), the first layer is alumina- and/or silica-rich, and the second layer is Ca₅Si₂O₈CO₃, Ca₅Si₂O₈CO₃ and/or Ca₇Si₆O₁₈CO₃.2H₂O.

In a ninth example of the first embodiment, the precursor particle/core is formed of (Ba_(0.6)Sr_(0.3)Ca_(0.1))TiO₃, the first layer is titania-rich, and the second layer is olekminskite Sr(Sr,Ca,Ba)(CO₃)₂.

As demonstrated in Table 2C, the second layer may also be modified by introducing additional anions and/or cations to the already CO₃ ⁻² anions present. Accordingly, the second layer may comprise a chemical composition including cations bonded with anions corresponding to one or more reactants. The cations associated with the chemical composition of the second layer may be bonded to the anions of a first reactant. The cations associated with the chemical composition of the second layer may be bonded to the anions of a reactant other than the first reactant. The cations associated with the chemical composition of the second layer may alternatively be bonded to the anions of a first reactant and to the anions of a second or more reactants. Such additional anions and cations may be used to modify the second layer to increase its physical and chemical properties such as fire resistance or acid resistance. For example, as shown in Table 2C, while the first layer is retained as a silica-rich layer, the second layer may be modified by adding extra anions or cations to the reaction. Some exemplary anions that may be added include PO₄ ⁻² and SO₄ ⁻². Other anions or cations may also be used. As demonstrated in Table 2C, the end results may include, for example, different phosphate, sulphate, fluoride bearing carbonates or combinations thereof. As in Table 2B, the examples provided in Table 2C are only exemplary and should not be viewed as limiting as they are not an exhaustive list of possibilities.

TABLE 2C Concept showing how by using wollastonite as a core particle, how different source of anions and/or cations, in addition to CO³⁻ ⁻² anions, can be used to generate modified encapsulating layers Core First Extra anion/cation Particle Layer source Encapsulating Layer Carbonate Type CaSiO₃ Silica Phosphates Ca₅(PO₄,CO₃)₃OH Phosphate bearing carbonates rich layer Sulphates Ca₂SO₄CO₃•4H₂O Sulphate bearing carbonates Fluorides Ca₂CO₃F₂ Fluorides bearing carbonates Phophates and Ca₅(PO₄,CO₃)₃F Fluoride and phosphates fluorides bearing carbonates Mg⁺² source like CaMg(CO₃)₂ Multiple cation carbonates chlorides, nitrates, hydroxides etc. A combination of Ca₆Mg₂(SO₄)₂(CO₃)₂Cl₄(OH)₄•7H₂O Post-1992 Carbonate Bearing cation and anion Minerals sources

In a further exemplary embodiment, a precursor particle may be formed predominately of copper and may be reacted with water transforming a peripheral portion of the precursor particle into a first layer formed predominantly of copper hydroxide. Next, carbon dioxide may be used to transform a peripheral portion of the first layer into a predominantly copper carbonate second layer. The presence of the second layer on the first layer acts as a barrier to further reaction between carbon dioxide and the copper, thus resulting in the bonding element having the core, first layer and second layer. In this example, elemental copper is in the core, and the combination Cu²⁺ and OH⁻ to form copper hydroxide constitute the first layer, and the combination of Cu²⁺ and CO₃ ²⁻ to form copper carbonate constitute the second layer.

A similar result may also be achieved in a modified exemplary embodiment in which the precursor particle may be formed predominately of copper oxide. The precursor particle is then reacted with water transforming a peripheral portion of the precursor particle into a first layer formed predominantly of copper hydroxide. Next, carbon dioxide may be used to transform a peripheral portion of the first layer into a predominantly copper carbonate second layer. The presence of the second layer on the first layer acts as a barrier to further reaction between carbon dioxide and the copper, thus resulting in the bonding element having the core, first layer and second layer. In this modified example, copper is also present in the core, the combination of Cu²⁺ and OH⁻ into copper hydroxide constitute the first layer, and the combination of Cu^(2±) and CO₃ ²⁻ into copper carbonate constitute the second layer. Thus, in these exemplary embodiments, the core and the first and second layers all have the same cationic species but different anions.

In a further exemplary embodiment, a precursor particle formed predominately of bronze reacts with water transforming a peripheral portion of the precursor particle into a first layer including copper hydroxide. Next, carbon dioxide transforms a peripheral portion of the first layer into second layer including copper carbonate. The presence of the second layer on the first layer acts as a barrier to further reaction between carbon dioxide and the bronze, thus resulting in the bonding element having the core, first layer and second layer.

In yet a further exemplary embodiment, a precursor particle may also be formed of a material other than copper or bronze. The precursor material may be one selected from the previously discussed list. For example, the precursor material may comprise silicon. The precursor may alternatively comprise aluminum. The precursor material may otherwise comprise iron. The precursor could than react to form a hydroxide as the first layer. Thus, for example, the first layer may be formed of a silicon hydroxide. Alternatively, the first layer may comprise an aluminum hydroxide. The first layer might instead comprise an iron hydroxide. Furthermore, instead of a hydroxide, the first layer may comprise an oxide. For example, the first layer may comprise a silicon oxide. In the alternative, the first layer may comprise aluminum oxide. In yet another alternative, the first layer may comprise an iron oxide. Similarly, the second layer may constitute a carbonate as discussed above. Thus, for example, the second layer may comprise silicon carbonate. In the alternative, the second layer may comprise aluminum carbonate. In yet another embodiment, the second layer may comprise iron carbonate. As discussed above, other precursors materials may be used, thus these compositions of core, first layer, and second layer are simply exemplary and should not be viewed as limiting.

Process of Forming the Bonding Elements

The above-described bonding elements may be formed, for example, by a method of gas-assisted hydrothermal liquid phase sintering. In this method, a porous solid body including a plurality of precursor particles is exposed to a solvent, which partially saturates the pores of the porous solid body, meaning that the volume of the pores are partially filled with water.

In some systems such as carbonate forming ones, completely filling the pores with water is believed to be undesirable because the reactive gas is unable to diffuse from the outer surface of the porous solid body to all of the internal pores by gaseous diffusion. Instead, the reactant of the reactive gas would dissolve in the liquid and diffuse in the liquid phase from the outer surface to the internal pores, which is much slower. This liquid-phase diffusion may be suitable for transforming thin porous solid bodies but would be unsuitable for thicker porous solid bodies.

A gas containing a reactant is introduced into the partially saturated pores of the porous solid body and the reactant is dissolved by the solvent. The dissolved reactant then reacts with the at least first chemical element in the precursor particle to transform the peripheral portion of the precursor particle into the first layer and the second layer. As a result of the reaction, the dissolved reactant is depleted from the solvent. Meanwhile, the gas containing the reactant continues to be introduced into the partially saturated pores to supply additional reactant to the solvent.

As the reaction between the reactant and the at least first chemical element of the precursor particles progresses, the peripheral portion of the precursor particle is transformed into the first layer and the second layer. The presence of the first layer at the periphery the core eventually hinders further reaction by separating the reactant and the at least first chemical element of the precursor particle, thereby causing the reaction to effectively stop, leaving a bonding element having the core as the unreacted center of the precursor particle, the first layer at a periphery of the core and a second layer on the first layer.

As a result of the transformation, the core has the same or similar shape as the precursor particle but smaller in size, the first layer and the second layer may each have uniform or non-uniform thickness that partially or fully coat the core and could be porous layer depending on the size and shape of the pores that surrounded the precursor particle during the transformation process. The resulting bonding element comprising the core, the first layer and the second layer, is generally larger in size than the precursor particle, filling in the surrounding porous regions of the porous solid body and possibly bonding with adjacent materials in the porous solid body. As a result, net-shape formation of products may be formed that have substantially the same size and shape as but a higher density than the porous solid body. This is an advantage over traditionally sintering processes that cause shrinkage from mass transport to produce a higher density material than the initial powder compact.

Without being limited by theory, the transformation of the precursor core may be effected because at least a first chemical element is leached out from the precursor particle into the solvent, leaving a depletion zone, which generally excludes the first chemical element except for a finite concentration that forms the first layer. The leached first chemical element is then combined with the reactant of the solvent to form the second layer. The presence of the first and second layers at the periphery the precursor core eventually hinder further reaction by separating the introduced reactant and the first chemical element of the precursor particle, thereby limiting the reaction to a very slow reaction rate that may be halted for practical, leaving a bonding element having the core, the first layer at a periphery of the core and a second layer on the first layer. Another theory is that the multiple chemical elements of the precursor particle are dissolved into the solvent and a first chemical element is precipitated to form the first layer and thereafter remaining cations are precipitated to form the second layer.

In one example of the method of gas-assisted hydrothermal liquid phase sintering, a porous solid body comprising a plurality of precursor particles is placed in an autoclave chamber and heated. Water as a solvent is introduced into the pores of the porous solid body by vaporizing the water in the chamber. A cooling plate above the porous solid body condenses the evaporated water that then drips onto the porous body and into the pore of the porous solid body, thus partially saturating the pores of the porous solid body. However, the method of introducing water in this example is one of several ways that water can be delivered. In another example, the water can be heated and sprayed.

Meanwhile, carbon dioxide as a reactant is pumped into the chamber, and the carbon dioxide diffuses into the partially saturated pores of the porous body. Once in the pores, the carbon dioxide dissolves in the water, thus allowing the reaction between the precursor particles and the carbon dioxide to transform the peripheral portions of the precursor particles into the first and second layers.

In a second embodiment, the precursor particle comprises one or more chemical elements, such as a ceramic material or a metallic material. During the transformation process, a first reactant associated with the liquid reacts with at least a first chemical element in the ceramic or metallic material to form the first layer. A second reactant associated with the liquid then reacts with the first chemical element in a peripheral portion of the first layer to form the second, encapsulating layer. Accordingly, the core comprises the same chemical composition as the precursor particle, including the first chemical element. The first layer comprises a compound that is a combination of the first reactant and the first chemical element. The second layer comprises a compound that is a combination of the second reactant and the first chemical element.

Without being limited by method of manufacturing, the above-described bonding element may be formed by exposing the porous solid body including at least one precursor particle, such as copper, to a first reactant, such as water, to form the first layer by reaction of the water and the copper. Subsequently, a method of gas-assisted hydrothermal liquid phase sintering may be performed. In this method, the core and first layer are exposed to a solvent (such as water), which may or may not initially have a second reactant dissolved therein that reacts with the precursor particle. Meanwhile, a gas containing additional amounts of the second reactant is introduced into the porous solid structure, thereby supplying the second reactant to the solvent for further reaction with the precursor particle.

As the reaction between the second reactant and the first layer progresses, the second reactant continues to react with the first layer, transforming the peripheral portion of the first layer into the second layer. The formation of the second layer may be by the exo-solution of a component in the first layer, and such a second layer may be a gradient layer, wherein the concentration of one of the chemical elements (cations) making up the second layer varies from high to low as you move from the core particle surface to the end of the first layer. It is also possible that the second layer can be a gradient composition as well, such as when the layers are either amorphous or made up of solid solutions that have either constant or varying compositions.

The presence of the second layer at the periphery the precursor core eventually hinders further reaction by separating the second reactant and the first layer, causing the reaction to effectively stop, leaving a bonding element having the core, the first layer at a periphery of the core and a second layer on the first layer. The resulting bonding element is generally larger in size than the original precursor particle, thereby filling in the surrounding porous regions of the porous solid body and bonding with adjacent materials of the porous solid body. As a result, the method allows for net-shape formation of products having substantially the same shape as but a higher density than the original porous solid body. This is an advantage over traditionally sintering processes that cause shrinkage from mass transport to produce a higher density material than the initial powder compact.

Bonding Matrix

The bonding matrix, in accordance with exemplary embodiments of the present invention, comprises a plurality of bonding elements, as previously defined. The bonding matrix may be porous. As explained above, the degree of porosity depends on a number of variables that can be used to control porosity, such as temperature, reactor design, the precursor material and the amount of liquid that is introduced during the transformation process. Thus, depending on the intended application, the porosity can be set to almost any degree of porosity from about 1 vol % to about 99 vol %.

Composite Material

The bonding matrix may incorporate filler material, which would be mixed with the precursor material during the transformation process described above, to create a composite material.

In general, the filler material may include any one of a number of types of materials that can be incorporated into the bonding matrix, such as, for example, an inert material and active material. The inert material is a material that does not go through any chemical reaction during the transformation and does not act as a nucleation site. The active material may consist of a first type that does not go through any chemical reaction during the transformation but acts as a nucleation site and/or a second type that chemically reacts with the bonding matrix during the transformation.

As explained above, the inert material does not go through any chemical reaction during the transformation and does not act as a nucleation site, although it may physically or mechanically interact with the bonding matrix. The inert material may involve polymers, metals, inorganic particles, aggregates, and the like. Specific examples may include, but are not limited to basalt, granite, recycled PVC, rubber, metal particles, alumina particle, zirconia particles, Carbon-particles, carpet particles, Kevlar™ particles and combinations thereof.

As explained above, the first type of active material does not go through any chemical reaction during the transformation but acts as a nucleation site. Additionally, it may physically or mechanically interact with the bonding matrix. For example, when using a bonding element that has a carbonate phase as the second layer, this type of active material may include, for example, limestone, marble dusts and other calcium carbonate-containing materials.

As explained above, the second type of active material chemically reacts with the bonding matrix during the transformation. For example, magnesium hydroxide may be used as a filler material and may chemically react with a dissolving calcium component phase from the bonding matrix to form magnesium calcium carbonate.

More will be said about the use of filler material in conjunction with the bonding matrix, and how the addition of filler material may further improve the function, i.e., material properties, of the resulting composite material.

The bonding matrix may occupy almost any percentage of the resulting composite material. Thus, for example, the bonding matrix may occupy about 1 vol. % to about 99 vol. % of the composite material. Accordingly, the volume fraction of the bonding matrix can be less than or equal to about 90 vol. %, such as 70 vol. %, such as 50 vol. %, such as 40 vol. %, such as 30 vol. %, such as 20 vol. %, such as less than or equal to about 10 vol. %. A preferred range for the volume fraction of the bonding matrix is about 8 vol. % to about 99 vol. %, most preferred range of about 8 vol. % to 30 vol. %.

The composite material, including the bonding matrix and the filler, may also be porous. As explained above, the degree of porosity depends on a number of variables that can be used to control porosity, such as temperature, reactor design, the precursor material, the amount of liquid that is introduced during the transformation process and whether any filler is employed. Thus, depending on the intended application, the porosity can be set to almost any degree of porosity from about 1 vol % to about 99 vol %. For example, the porosity may be less than or equal to about 90 vol. %, such as 70 vol. %, such as 50 vol. %, such as 40 vol. %, such as 30 vol. %, such as 20 vol. %, such as less than or equal to about 10 vol. %. A preferred range of porosity for the composite material is about 1 vol. % to about 70 vol. %, most preferably between about 1 vol. % and about 10 vo. % for high density and durability and between about 50 vol. % and about 70 vol. % for lightweight and low thermal conductivity.

Bonding Matrix Orientation

Within the bonding matrix, the bonding elements may be positioned, relative to each other, in any one of a number of orientations. As such, the bonding matrix may exhibit any one of a number of different patterns. For example, the bonding elements can be oriented in one direction (i.e., a “1-D” orientation), in two directions (i.e., a “2-D” orientation) or three directions (i.e., a “3-D” orientation). Alternatively, the bonding elements may be oriented in a random pattern (i.e., a “random” orientation).

Aforementioned and other bonding element orientation can be achieved by any one of a number of processes. These processes including, but are not limited to, tape casting, extrusion, magnetic field and electric field casting. However, it will be understood that pre-forming the precursor in accordance with any one of these methods would occur prior to transforming the precursor particle according to the transformation method described above. One of ordinary skill would understand how to orient the bonding elements.

Moreover, the concentration of bonding elements in the bonding matrix may vary. For example, the concentration of bonding elements on a volume basis may be relatively high, wherein at least some of the bonding elements are in contact with one another. This situation may arise if filler material is incorporated into the bonding matrix, but the type of filler material and/or the amount of filler material is such that the level of volumetric dilution of the bonding element is relatively low. In another example, the concentration of bonding elements on a volume basis may be relatively low, wherein the bonding elements are more widely dispersed within the bonding matrix such that few, if any of the bonding elements are in contact with one another. This situation may arise if filler material is incorporated into the bonding matrix, and the type of filler material and/or the amount of filler material is such that the level of dilution is relatively high. Further yet, the concentration of bonding elements on a volume basis may be such that all or almost all of the bonding elements are in contact with one another. In this situation, no filler material may have been added, or if filler material was added, the type of filler material and/or the amount of filler material is such that the level of volumetric dilution is almost non-existent.

FIGS. 2(a)-2(d) illustrate a bonding matrix that includes fiber- or platelet-shaped bonding elements in different orientations possibly diluted by the incorporation of filler material, as represented by the spacing between the bonding elements. FIG. 2(a), for example, illustrates a bonding matrix that includes fiber-shaped bonding elements aligned in a 1-D orientation, e.g., aligned with respect to the x direction. FIG. 2(b) illustrates a bonding matrix that includes platelet-shaped bonding elements aligned in a 2-D orientation, e.g., aligned with respect to the x and y directions. FIG. 2(c) illustrates a bonding matrix that includes platelet-shaped bonding elements aligned in a 3-D orientation, e.g., aligned with respect to the x, y and z directions. FIG. 2(d) illustrates a bonding matrix that includes platelet-shaped bonding elements in a random orientation, wherein the bonding elements are not aligned with respect to any particular direction.

FIGS. 2(e)-2(f) illustrate a bonding matrix that includes platelet-shaped bonding elements in two different orientations and concentrations. FIG. 2(e), for example, illustrates a bonding matrix that includes a relatively high concentration of platelet-shaped bonding elements that are aligned in a 3-D orientation, e.g., aligned with respect to the x, y and z directions. The relatively high bonding element concentration is illustrated by the lack of filler material around the bonding elements; thus, there is little to no dilution of the bonding elements. In contrast, FIG. 2(f) illustrates a bonding matrix that includes a relatively low concentration of platelet-shaped bonding elements that are situated in a random orientation. The relatively low bonding element concentration is illustrated by the presence of filler material around the bonding elements; thus, there is at least some dilution of the bonding elements. Due to the concentration and orientation of the bonding elements in FIG. 2(f), the composite material may be referred to as a percolation network. The composite material of FIG. 2(f) achieves the percolation threshold because a large proportion of the bonding elements are touching one another such that a continuous network of contacts are formed from one end of the material to the other end.

The percolation threshold is the critical concentration above which bonding elements show long range connectivity with either a ordered (FIG. 2(e)) or random orientation (FIG. 2(f)) of bonding elements.

In addition to orientation and concentration, the bonding elements in the bonding matrix can be arranged such that they exhibit a certain connectivity pattern with the filler material. Such connectivity patterns are described in, for example, Newnham et al., “Connectivity and piezoelectric-pyroelectric composites”, Mat. Res. Bull. Vol. 13, pp. 525-536, 1978).

FIG. 3 illustrates a number of different connectivity patterns for an exemplary composite material including connectivity patterns 0-0, 1-0, 2-0, 3-0, 1-1, 2-1, 3-1, 2-2, 3-2, 3-2, 3-3 and 3-3. In FIG. 3, the exemplary composite material has two components, a first (shaded) component which may represent the bonding matrix, and a second (un-shaded) component that may represent filler material. The different types of connectivity patterns can be exploited to achieve desired material properties associated with the composite material.

FIGS. 4(a)-4(b) illustrate examples of a composite material that comprises a bonding matrix (white portion) and equiaxed filler particles or anisotropic fibers, respectively. In the case of FIG. 4(a), the equiaxed filler particles are arranged in a random orientation, whereas the bonding matrix is aligned along all three axes. Thus, it can be said that the connectivity pattern of the composite material in FIG. 4(a) is a 3-0 connectivity pattern. In the case of FIG. 4(b), the anisotropic filler fibers are arranged in 1-D orientation with respect to the z direction. Thus, it can be said that the connectivity pattern of the composite material in FIG. 4(b) is a 3-1 connectivity pattern. Again, depending on the application and the desired material properties, the filler material may be any one of a plurality of inert and/or active materials.

Hierarchical Structure

Different types of bonding matrices can be created by varying the matrix porosity and by incorporating core fibers of different sizes (as seen in Tables 3 and 4 below). If FB1 composition is an example of bonding matrix (Table 3), this bonding matrix can be used to form repeating 1, 2, 3, 4, or higher levels of hierarchic structures. The level of hierarchic structure can refer to the number of length scales where an important structural feature is introduced (FIGS. 13(a)-13(d)). Different kinds of particulate and fiber components can be used with, for example, 1-, 2-, 3-, or higher level hierarchic structures to fabricate different kinds of structures with different connectivity as shown in FIG. 3.

TABLE 3 Variation of compressive strength in different bonding matrices formed by using different core fiber dimensions Com- pressive Com- Strength position Median fiber size (d50) (MPa) FB1A 9 μm (as-given by manufacturer, NYAD 400) 163 ± 8  FB1B 9 μm (as-given by manufacturer, NYAD 400) 147 ± 24  FB2 15 μm (as-given by manufacturer, NYAD M200 136 ± 6  FB3 70 μm (as-given by manufacturer, NYAD M100) 60 ± 14 FB4 30 vol. % (−7 to +14 mesh 72 (~1400-2800 μm) of NYCOR 100), 30 vol. % (−14 to +100 mesh (~1400-150 μm) of NYCOR 100), and 40 vol % (−400 mesh, NYAD 400)

TABLE 4 Effect of porosity of bonding elements fabricated with fiber cores of d₅₀ = 9 μm on compressive strength Porosity Compressive Composition (%) Strength (MPa) P1 45 10 P2 38 40 ± 5  P3 23 110 ± 10  FB1A 17 163 ± 8 

Hierarchy describes how structures form patterns on several length scales. The examples described above are but one example of how the bonding elements may be hierarchically employed in a manner that can promote dense packing, which provides for making a strong material, among other potential useful, functional purposes.

An illustration of the multilevel repeating hierarchic structure is shown in FIGS. 13(a)-13(d) wherein an ordered hierarchic structure can repeat at different length scales, such as 1 or more length scales.

For example, a 1-level repeating hierarchic system can be described as a composite formed by blending two different size or particle size ranges, generally differing by an order of magnitude. The larger size particles can arrange in different types of packing like Hexagonal Close Packing, or Cubic Close Packing, or Random Packing, but not limited to these, to form a network that contains interstitial void spaces, and the particles of smaller size can nestle in voids of particles of larger size. Ideally, these hierarchic systems can be prepared by using particles of same size in each level, for example spherical particles with 1 mm diameter are filling interstitial void spaces of packed spherical particles with 10 mm diameter. However, in practice, it is difficult to obtain mono-dispersed particles, consequently, hierarchic systems will be illustrated by using modal continuous distributions of particle size. For example, FB1B type bonding elements (d₅₀≈9 μm) can fit in the voids of filler particles of particle size varying between (100-500) μm (FIG. 13(a)). In order to further enhance connectivity of the bonding matrix in the structure, a coating of FB1B type bonding elements can also be applied to coarser filler particles and consequently these FB1B type bonding elements can fill the void spaces of coated coarser filler particles (FIG. 13(b)). Another alternative method of making 1-level hierarchic structure would be to use fine filler particles (<1 μm median particle size) in voids of FB1B bonding matrix.

For example, 2-level hierarchic system can be described as a composite of 1-level hierarchic system combined with larger or smaller particles whose particle size differs by an order of magnitude from either the coarser or finer particles in 1-level hierarchy. For example, in the present example, FB1B type bonding elements in voids of medium filler particles between (100-500) μm, and subsequently this 1-level hierarchic system uniformly distributed in voids of coarser 1-5 mm aggregates (FIG. 13(c)). In order to enhance connectivity of the bonding matrix further, a thin coating of FB1B bonding matrix (Table 3) can be applied on both coarser and medium filler particles (FIG. 13(d)).

For example, a 3-level hierarchic system can be described as a composite of 2-level hierarchic system combined with larger or smaller particles differing by an order of magnitude than either the largest or the smallest particle in 2-level hierarchy. For example, <1 micron fine filler particles in the voids of FB1B matrix forming a 1-level hierarchy, and subsequently this 1-level hierarchy in voids of larger filler particles between 100-500 μm forming a 2-level hierarchy, and finally this 2-level hierarchy in voids of 1-5 mm filler aggregates forming a 3-level hierarchy. Along the same line, a higher order, n level hierarchic system can be generated. As the levels of hierarchy increase, the range of length scales encompassing the various levels also increases. Thus, as n increases to infinity, so does the length scale. This huge range of length scale and hierarchy provides an infinite ways to deploy our novel bonding element in materials.

It is also possible to use bonding elements with different particles from different size fraction ranges to enhance packing by using non-repeating hierarchic or random packing systems also. As such, the organization of particles is either not repeating and hierarchic—some may consider this hierarchic in structure but having different structure in the geometric sense at different length scales, or random packing which implies particles are mixed randomly without incorporating non-random structures such as interstitial packing of large pores with fine particles or coatings of one particulate component on top of another.

These packing strategies can lead to high bulk densities, which can be manifested by small water absorption values. For example, water absorption of FB1B (Table 3) is 7.7±0.6 wt % (5 h boiling water test, ASTM C 67). If two components of different size ranges are used, for example, when FB1B Wollastonite fiber cores is blended with sand (CPC2, Table 12) packing is improved, and water absorption decreases to 5.3±0.5 wt %. Similarly, when particles from three size fractions are used, namely, FB1B Wollastonite fiber cores blended with sand (particle size between 300-500 microns) and basalt aggregates (particle size between 6-8 mm), water absorption is further decreased to 3.1±0.9 wt %. Alternatively, if 1 wt. % fumed silica (d₅₀<1 μm) is added in CPC2 type composition then water absorption is decreased further to 2.6 wt %.

Use of Bonding Matrix

The bonding matrix, including the bonding elements described above can be used to customize and, therefore, improve the material properties of almost any article that has a microstructure that can be modified by the incorporation of the bonding matrix, such as cement or concrete. In one example, the bonding matrix can be employed as a partial or complete substitute for Portland cement, and used as a hydrate-free bonding phase for components typically used in a wide range of concrete products, thereby improving various material properties associated with those products.

The material properties of the composite material that may be improved as a result of the incorporation of a bonding matrix, including bonding elements, in accordance with exemplary embodiments of the present invention, include mechanical properties, thermal properties and durability. However, specific mechanical, thermal and durability properties other than those listed in Table 19 may be improved as well. Additional material properties such as optical properties, electronic properties, catalytic properties, nuclear properties and magnetic properties may also be improved.

By way of example, a composite material comprising a bonding matrix in accordance with exemplary embodiments of the present invention may exhibit improved damage tolerance under compression. Hereinafter, exemplary wollastonite particles are generally referred to as having a fiber shape for simplicity. However, the wollastonite particles may have any generally anisotropic morphology, such as having an acicular or fiber like shape.

With reference to FIG. 9, a material composed of smaller wollastonite cores (Composition P3 in Table 4, FIG. 9) exhibits sudden brittle fracture due to stress in compression. However, with reference to FIG. 10 (Composition FB4 in Table 3, FIG. 10), the incorporation of the longer wollastonite fiber cores in bonding matrix causes a series of crack deflections to occur, where each deflection provides relief (i.e., “damage recovery”) of the stress accumulation, thereby delaying the onset of ultimate failure. Another way, in which the bonding matrix may sudden brittle failure with more gradual failure, is by employing a plurality of core particle sizes and fine filler particles in the encapsulating layer (FIG. 12(a)). For example, fine particles, such as silica particles, can be dispersed in a bonding matrix with porosity. With reference to compound FB4 in Table 3, the core may comprise particles of three different sizes at three volume fractions. A larger or smaller number of sizes (e.g., 2, 4, 5, 6, or more) or different volume fractions can be used. The bonding matrix can then act as a hydrate free cementing phase in the composite by binding to itself and the fine particles. Such a composite microstructure would allow for gradual failure, as demonstrated in FIG. 12(b).

In this example, the crack propagation mechanism is being altered because of the different interfaces formed in the bonding matrix. The core particle(s) can act as a crack deflector. Additionally, a first interface is formed between the core and the first layer, and a second interface is formed between the first layer and the encapsulating layer. The two different interfaces can have the same or different strengths. For example, the first interface can be higher interfacial strength (e.g., mechanical strength) than the second interface, and vice versa. As a result, after a crack is initiated and begins to propagate, the crack could be deflected from a stronger phase and instead propagate along the weaker interface, causing debonding therein.

It has been demonstrated that a composite material including the bonding matrix can exhibit improved mechanical properties as set forth in the present disclosure. Also, as demonstrated in Table 10, the article can have a higher thermal conductivity and a lower thermal expansion coefficient than conventional Portland cement. Furthermore, it is believe that various composite materials according to the present invention may also exhibit a wide range of properties, such as those shown in Table 5. It should be understood that exemplary embodiments of composite materials may also have properties corresponding to subsets of the ranges listed in Table 5. For example, embodiments may include composite materials that have a thermal expansion coefficient between 3×10⁻⁶1° C. and 15×10⁻⁶1° C. Exemplary embodiments of composite material may exhibit a thermal conductivity of greater than about 0.13 W/m.k, and less than about 196 W/m.k. Exemplary embodiments of composite material may exhibit a heat capacity between 6 and 900 J/mole.K. Exemplary embodiments of composite materials may exhibit a Vicker's hardness between about 1 GPa and 30 GPa. Further exemplary embodiments include composite materials that may exhibit a compressive strength varying between 14 to about 3,000 MPa and a flexural strength of less than about 380 MPa. Exemplary embodiments of composite materials may also exhibit creep strain of less than 60×10⁻⁶/psi. Exemplary embodiments of composite materials may exhibit Cl⁻ permeability of less than 700 C. Exemplary embodiments of composite materials may be self-reinforced and have a ball impact resistance greater than 6 J. Exemplary embodiments of composite materials may also be reinforced with steel fibers and have a ball impact resistance greater than 10 J. Moreover, exemplary embodiments of composite materials may exhibit combinations of the above sub-ranges of properties and/or of those ranges of properties listed in Table 5.

TABLE 5 Upper and lower limit of different properties of composite material in accordance with embodiments Lower Limit Upper Limit Mechanical Properties Compressive Strength 1 kPa 8-16 GPa¹ Flexural Strength 1 kPa 655 MPa² Hardness 1 kPa 147 GPa¹ Modulus of Elasticity 1 kPa 700-1200 GPa¹ Fracture Toughness 0.0008 66 (MPa · m^(1/2))³ Creep testing by 99% strain No deformation during C512-02 to failure the entire course of (construction materials) testing High Temperature — At 400 MPa and Creep⁴ 1800° C., creep rate less than 10⁻⁶s⁻¹ Impact Resistance — Will Pass ASTM (Construction Materials) E-1886 or ASTM E-1996, or Dade County Standard Impact Resistance — 250 tons per square (Armor) centimeter—shock pressure⁵ Ductility Brittle Metal like ductility Castability Ganulated powders Can be cast into complicated shapes or be self-flowing, or vibration assisted flows Thermal Properties Thermal Conductivity 0.03 2000¹ (W/m · K) Heat Capacity C_(p,m) 6 900 J/(mol · K) Thermal Expansion 1-2 15 (10⁻⁶° C./min) Max working Cryogenic 2927 temperature (° C.) (air) conditions (Note: MP of CaO) Fire Resistance — ASTM E119 or ASTM E 84 Max working Cryogenic 4215 temperature (° C.) conditions (Ar or inert atmosphere)⁶ Shock Resistance — Pass ASTM C484 (Construction Materials) Shock Resistance — 500° C. thermal (Refractory)⁷ quenching Durability Chloride Permeability >2000 Negligible permeability (Coulombs) ASTM C1202 Abrasion Resistance >2 mm Negligible wear ASTM C944 Freeze and Thaw 0 300 cycles or higher and retain DF of 100 (ASTM C666 for concrete) Freeze and Thaw 0 50 cycles or higher (ASTM C67) Acid Freeze Thaw 0 Pass one or both (C666 and C67) standards Shrinkage (ASTM C157) NA Negligible Shrinkage Sulphate resistance (ASTM Comparable Performance C150/C150M − 09/C1012) to OPC Equal or better than Type V cement (<0.04% expansion) alkali-silicate reaction Fail ASTM C1260 Negligible expansion (ASR) (ASTM C1260) UV Exposure (G 154) Will be No effect after 5000 h damaged by UV Salt Spray Resistance Fail the test Pass ASTM B117 (B 117) Water absorption 99 wt. % No water (5 h boiling water test) water absorption absorption Tribological Behavior Coefficient of Friction⁸ 0.02 1.05 Wear Rate (mm³/N · m) >1 <10⁻⁸ Optical Properties Albedo (Reflectivity)⁹ 0.04 0.9 Band Gap¹⁰ (eV) @ 300K 0 6.36 ¹http://www.matweb.com/search/DataSheet.aspx?MatGUID=d8d230a8d9664bc390199dab7bc56e1e&ckck=1 ²http://www.insaco.com/matpages/mat_display.asp?M=SIC-RB ³http://en.wikipedia.org/wiki/Fracture_toughness ⁴http://www.hexoloy.com/ ⁵http://www.physorg.com/news8947.html ⁶http://chemicalproperties.org/property/melting-point/ ⁷http://www.ferroceramic.com/Cordierite_table.htm ⁸Kurt Kleiner (Nov. 21, 2008). “Material slicker than Teflon discovered by accident”. http://www.newscientist.com/article/dn16102-material-slicker-than-teflon-discovered-by-accident.html. Retrieved Dec. 25, 2008. ⁹http://en.wikipedia.org/wiki/Albedo#cite_note-heat_island-0 ¹⁰Evans, D A; McGlynn, A G; Towlson, B M; Gunn, M; Jones, D; Jenkins, T E; Winter, R; Poolton, N R J (2008). “Determination of the optical band-gap energy of cubic and hexagonal boron nitride using luminescence excitation spectroscopy”. Journal of Physics: Condensed Matter 20: 075233. doi:10.1088/0953-8984/20/7/075233.

Applications

The presently described bonding matrix and/or bonding element can be used in a variety of applications. Because of the superior properties of these bonding element/matrix as described herein, the element/matrix can be used in applications in electronic, optical, magnetic, biomedical, biotechnological, pharmaceutical, agricultural, electrochemical, energy storage, energy generation, aerospace, automotive, body and vehicle armor, textile, and abrasive and cutting applications, and any combination of foregoing applications. It can also be used as photochemical, chemical separations, photoelectric, thermionic and/or electroluminescent materials.

Some of the illustrative examples are provided below:

The bonding element or matrix can be used as a cementitious phase like Portland Cement, lime cement, or related cementitious materials. These solids can be applied in any applications of Portland Cement, lime cement or related cementitious materials.

The bonding element/matrix can be blended with additives, including CaCO₃, or gypsum, and sand, to form monolithic solids. Monolithic solids are solids that are formed as a single piece, without joints or seams. For the purposes of this specification, the term “monolithic” is not being used or intended to be used to describe uniformity at a microscopic level. Examples of the monolithic solids can mimic and/or resemble the performance as well as the appearance of Terracotta, or natural stones, such as granite and limestone. The appearance can be created by further forming different colors and textures with additives. In one embodiment, these monolithic solids can be used in any applications wherein conventional Terracotta, or natural stones are employed.

The bonding element or matrix can also be blended with sand, or other minerals to prepare mortar or grout, and the resultant material can be used in any applications wherein conventional mortar and grout are employed.

The bonding element/matrix can also be blended with metallic, or organic, or ceramic fibers to make a fiber cement. The resultant material can be used in any applications wherein conventional fiber cements are employed.

The bonding element or bonding matrix can be used in hydrate-free concrete applications. In one embodiment, it can be blended with sand and aggregate and/or aggregates to form a material that mimics and/or resembles regular or structural concrete. The resultant material can be used in any applications wherein conventional structural or regular concrete are employed, e.g., dams, bridges, swimming pools, homes, streets, patios, basements, balustrades, plain cement tiles, mosaic tiles, pavement blocks, lamp-posts, drain covers, or combinations thereof.

By careful sizing of the particles, dispersants, and/or wastes, such as cork, glass aggregates, resultant materials that mimic and/or resemble High Strength Concrete (HSC), 3D fiber type structures (e.g., concrete clothes), Rapid Strength Concrete (RSC), cork based composites, glass concrete, and High Performance Concrete (HPC) can be produced. The resultant material can be used in any applications in which conventional HSC, concrete clothes, RSC, cork based composites, glass concrete, HPC are employed.

Steam and/or vacuum during process can be further used to produce material that mimics/resembles Vacuum Concrete (VC) and that can be used in any applications in which conventional VC is used. In one alternative embodiment, by controlling the porosity, a resultant material that mimics/resembles Pervious Concrete can be produced. The material can be used in any applications, in which conventional Pervious Concrete is employed.

In one embodiment, the bonding element/matrix is blended with fibers, sand, aggregates, and/or other additives, such as defoamers and/or ultrafine particles, such as fumed silica and CaCO₃, to prepare fiber reinforced concrete (FRC) which performs like Fiber reinforced composites and/or Ultra High Performance Concrete (UHPC). These solids can be used in any applications, in which conventional FRC and/or UHPC is employed. In an alternative embodiment, by controlling the fluidity (e.g., by tailoring the water content during processing), other installation types of concrete products can be produced. The products included Shotcrete, Self Compacting Concretes, Roller Compacted Concretes, or combinations thereof.

In another embodiment, the bonding element/matrix is blended with a metal such as aluminum and Ca(OH)₂ and autoclaved, or by controlling porosity by using different aids like vacuum, or air entrainment to produce a material that mimics/resembles Autoclave Aerated Concrete (AAC). This material can be used in any applications in which conventional AAC is employed.

In an alternative embodiment, the bonding element/matrix is blended with sand and/or low density aggregates (e.g., expanded vermiculite and perlite, pumice, expanded slag, expanded shale, or combinations thereof), and by controlling porosity, these composites can be used as light-weight concretes or Cellular concrete, light-weight aerated concrete, variable-density concrete, foamed concrete or ultra-light-weight concretes or any other material related to these types of concretes. In another embodiment, the bonding element/matrix is blended with high density aggregates (e.g., density>3.2 g/cm³), and the resultant product can be heavy-weight concretes.

The presently described bonding element/matrix can be used in combination (and thus reinforced) with steel to make reinforced concrete material, which can be used in any applications in which reinforced concrete structures are employed. The material can be pre-stressed to mimic/resemble Pre-stressed Concrete. In one embodiment, the bonding element/matrix can be poured in huge blocks to produce a material that mimics/resembles mass concrete. Applications for these mass-concrete types of material can include gravity dams, large breakwaters, or a combination thereof. The concrete derived from the presently described bonding element/matrix can also be fabricated with different textures for decorative purposes.

In some embodiments, a composite material comprising the presently described bonding element/matrix can have superior properties. For example, it can have excellent corrosion resistance, such as providing protection to steel reinforcement in an environment with high chloride content, and excellent durability in aggressive sulphate environments. A composite material can be used in highly specialized applications, such as sound shielding and/or or nuclear radiation shielding. In one embodiment, the material can have desirable fire resistance, and can be suitable for refractory applications. The material can also withstand extreme weather conditions, such as, for example, freezing conditions, high temperatures in deserts, or extreme weather fluctuations, and/or freeze-thaw resistance. The material can also be suitable for use in specialized marine, cryogenic, and/or blast resistance applications. In some embodiments, the material can be used in earthquake resistant structures and/or geosynthetic type structures.

NON-LIMITING WORKING EXAMPLES Example 1

FIGS. 5a and 5b show secondary electron (SE) and back scattered electron (BSE) SEM images of randomly oriented CaSiO₃ core fibers coated by predominantly amorphous silica, and these coated fibers are encapsulated with CaCO₃ particles. Chemical mapping by EDS in FESEM of the microstructure showed wollastonite core fibers are coated by SiO₂ rich regions and encapsulated by CaCO₃ particles (FIG. 6). Different elements of bonding matrix are held together by CaCO₃ particles. XRD of this composition revealed that CaSiO₃ and CaCO₃ (calcite) are crystalline phases whereas silica rich regions are amorphous.

Table 6 compares mechanical properties of conventional monolithic materials with different compositions (Tables 3 and 4) formed by using a wollastonite core fiber-based bonding matrix. These bonding matrices showed a range of compressive strengths between 40 and 300 MPa. Moreover, compressive strength can be tailored by both the fiber core unit size and porosity. The highest strength observed in this bonding matrix has a comparable strength to a dimension stone like granite. FB1A and FB1B samples were prepared by pressing and casting forming methods, respectively, prior to conducting the disproportionation reaction. These two different ceramic forming techniques lead materials with slightly different compressive strengths because of different ways the raw materials pack (Table 3). In addition, FB1A matrix based smaller samples (diameter=12.8 mm) an average strength of 298±5 MPa has been observed. These results indicate that it is possible to further enhance strength in these solids by reducing the defect populations further by more advanced processing. There are many conventional methods of powder processing that can be used to reduce the defect populations and in turn allow larger samples to results that have these improved mechanical properties. This process of optimization is possible with someone of ordinary skill given the use of this novel bonding element technology.

TABLE 6 Comparison of compressive strength of different materials Material Compressive Strength (MPa) Chalk¹ 3-4 Portland Cement² 30-50 Marble³ 50 Granite³ 130-200 Limestone³ 12 Terracotta⁴ 65 Bonding Matrix (Tables 3 and 4)  40-300 ¹Anne Duperret, Said Taibi, Rory N. Mortimore, Martin Daigneault, Effect of groundwater and sea weathering cycles on the strength of chalk rock from unstable coastal cliffs of NW France”, Engineering Geology 78 (2005) 321 343. ²S. Mindess, J. F. Young, and D. Darwin, Concrete, Second Edition, Prentice Hall (2003). ³http://www.supremesurface.com/granite/granite.html, ⁴http://content.wavin.com/WAXUK.NSF/pages/Terracotta-Performance-Data-EN/$FILE/performance_data.pdf

FIG. 7 shows a Vicker's Hardness Indentation on a composite material with microstructure described in Example D (composition P3, Table 4). This composite material had a hardness of −1.6 GPa. Cracks emanating from the corner of the indentation were studied subsequently to understand crack propagation (FIG. 8(a)). B and D regions show that the crack has deviated around different fiber shaped wollastonite core fibers by debonding in the interface between silica rich and CaCO₃ rich regions (FIG. 8(a)). These core fibers act as crack deflectors, and cracks subsequently deviated around them and propagated through CaCO₃ rich phases present at interface boundaries (FIG. 8(b)). Accordingly, the interface between coated silica and CaCO₃ rich region is weak, as compared to robust interface between core wollastonite grain and silica phase coating (FIG. 8(c)). This unique interface structure can be used to design structures in which cracks are deflected by debonding which increases the damage tolerance of these structures against sudden brittle failure. P3 composition showed brittle failure and had a compressive strength of 110 MPa (FIG. 9) and a tensile strength of 12 MPa.

It is further possible to tailor the hardness of these composite materials by making composite materials with different additives like carbides, silicates, glass, and glass ceramics or even different types of metals and polymers. For simplicity, hardness calculations are done by assuming 30 vol. % P3 bonding matrix blended with different additives, and subsequently, by using a rule of mixture calculation, different range of hardness values can be calculated. For example, by adding BeO, a hardness of 1-1.3 GPa can be achieved, and by adding B₄C, a hardness of 21-27 MPa can be achieved also as shown in the Table 7. In other exemplary embodiments the material can have a Vicker's Hardness between about 1 GPa and about 30 GPa.

TABLE 7 Summary of calculated hardness values of different composites made with P3 Bonding Elements. 30 Vol. % P3 Single Phase Bonding Elements Hardness Added Material (GPa) Hardness (GPa) Oxides Al₂O₃ 19.0-26.0 14-19 BeO 0.8-1.2 1.0-1.3 MgO  6.0-10.0 4.7-7.5 MgAl₂O₄ 14.0-18.0 10.0-13.0 Mullite 15 11.0 SiO₂ (Quartz) 12.0 (011) 8.9 TiO₂  9.0-10.0 6.8-7.5 ThO₂ 10 7.48 Y₂O₃ 7.0-9.0 5.4-6.8 Y₃Al₅O₁₂ 17.0-19.0 12.4-13.8 ZnO 1.3-3.3 1.4-2.8 ZrSiO₄ 15 11.0 ZrO₂ (cubic) 12.0-15.0  9.0-11.0 ZrO₂ (Partially Stabilized) 13 9.6 Carbides, Borides, Nitrides and Silicides AlN 12 8.9 B₄C 30.0-38.0 21-27 SiC (hot pressed) 26.0-36.0 19-26 Si₃N₄ (hot pressed) 17.0-30.0   12-21.5 TiB₂ 18.0-34.0 13-24 TiC 16.0-28.0 11.0-20.0 ZrB₂ 22 16.0 Halides and Sulfides CaF₂ 1.8 1.7 KCl 0.12 0.56 MgF₂ 6 4.68 SrF₂ 1.4 1.46 Glass and Glass Ceramics Aluminosilicates (Corning 1720) 6.6 5.1 Borosilicates (Corning 7740) 6.5 5.0 Silica (Fused) 6.0-9.0 4.7-6.8 Soda lime silica glass 5.5 4.3

Similarly, the bonding elements may be also employed to affect the thermal conductivity. Also, the bonding elements may be used to affect the thermal expansion. Exemplary embodiments of these variations are provided in Table 8.

TABLE 8 Summary of calculated thermal conductivity and thermal expansion of different composites made with P3 Bonding Elements [1-6] 30 Vol. % P3 Bonding Pure Element Added Thermal Thermal Thermal Thermal Conductivity Expansion Conductivity Expansion Materials (W/m · k) 10⁻⁶/° c. (W/m · k) 10⁻⁶/° C. Granite 3.1 7.0-9.0 2.68   6-7.5 Basalt 1.4 6.0-8.0 1.49 5.0-7.0 Limestone 3.1 6 2.68 5.4 Dolomite 3.6  7.0-10.0 3.03 6.0-8.0 Sandstone 3.9 11.00-12.00 3.24  9.0-10.0 Quarzite 4.3 11.0-13.0 3.52  9.0-10.0 Marble 2.7 4.0-7.0 2.4 4.0-6.0 Vermiculite 0.06 NA 0.55 NA Cork 0.07 0.56 Wool 0.04 0.54 Perlite 0.03 0.53 Nano-aerogel¹¹ 0.009-0.012 0.51-0.52 Rice Hulls 0.03-0.06 0.53-0.55 Cotton 0.03 0.531 Diamond 1000-2000  700-1400 Cement Paste w/c = 0.4 1.3 18.0-20.0 1.42 14.0-15.0 w/c = 0.5 1.2 18.0-20.0 1.35 14.0-15.0 w/c = 0.6 1 18.0-20.0 1.21 14.0-15.0 Concrete 1.5-3.5 7.4-13  1.5-3.0  6.0-10.0 Water 0.5 — 0.86 — Air 0.03 — 0.531 — Steel 120 11.0-12.0 84.51  9.0-10.0 AlN 200.0-280.0 5.6 140.0-196.0 5.12 BeO  63.0-216.0 8.5-9.0  44.00-152.00 7.0-7.5 MgO 37 13.5 26.41 10.65 Si₃N₄ 25 3.1-3.7 18.01 3.4-3.8 TiB₂ 40 7.8 28.51 6.66

Tables 3-4 show how compressive strength varies with core fiber size. As the mean size of core fibers was decreased from 70 to 9 microns, the compressive strength increased from 60 to as high as 300 MPa but stress versus displacement curves such as in FIG. 9 show that these materials undergo catastrophic brittle fracture (not graceful failure).

Composition FB4 is developed by using very large core fibers (˜2800-150 μm) of different size fractions to impart damage tolerance. Initially during stress versus displacement measurement (FIG. 10), stress varied linearly with displacement. After reaching an ultimate compressive strength (UCS) of 72 MPa, stress dropped sharply due to failure, thereafter sample regained its original strength (a sign of damage tolerance or in other words, graceful failure or ductility or ductile failure); subsequently this cycle continued 3 times before failure. Thus, the interfacial structure played a major role in damage tolerance of this bonding matrix (FIG. 10). These kinds of structures will be referred as “Self Reinforced Cementitious Composites (SRCC)”. In this case the novelty is that fiber-based bonding elements are acting as both cementitious units (active fibers or filler), as well as, they are also acting as crack deflectors for damage tolerance.

In summary, sizes of core fibers play a major role in controlling the mechanics of the bonding matrix. If mean particle size of core fibers are small (about <70 μm) then these bonding matrices showed large compressive strengths (as high as 300 MPa) with brittle rather than graceful fracture or failure. If large core fibers (˜150-2800 μm) are used (composition FB4, Table 3) then crack deflection and debonding of these large active fiber interfaces play an important role in inducing damage tolerance (or ducility or graceful failure).

By controlling porosity in randomly oriented bonding matrix composed of wollastonite core fibers with mean particle size of 9 μm, a wide variety of structures can be created. Table 4 shows the effect of porosity on compressive strength of bonding matrix. The decrease in porosity from 45% to 17% in the bonding matrix caused an increase in compressive strength of the bonding matrix from 10 MPa to 163 MPa.

The above example shows how the properties of these materials can be changed. There are many microstructures where this bonding element may be used.

Example 2

FIGS. 11(a)-11(d) show interaction of SiO₂, high Ca Fly Ash (HCFA) and CaCO₃ with P3 bonding matrix (P3 composition, Table 4). Observation of the P3 bonding matrix and SiO₂ interface (FIGS. 11(a) and (b)) reveals that CaCO₃ particles and silica-rich coating around wollastonite core fibers have formed a bonded interface with externally added silica particles. In P3 bonding matrix-HCFA interface there was no sign of debonding between the HFCA and bonding matrix (FIG. 11(b)). Similarly in P3 bonding matrix-CaCO₃ interface, externally added CaCO₃ particles have formed diffuse interfaces with bonding elements.

FIG. 12(a) shows a typical example of 0-3 composite, where 70 vol. % sand (silica) particulate components are dispersed in P3 bonding matrix with porosities in the structure (Table 4). This composite material showed a gradual failure during compression, and had a compressive strength of ≈55 MPa (FIG. 12(b)). 30 vol. % P3 bonding matrix is acting as the hydrate free cementing phase in the composite material by binding to itself as well as to sand particles.

FIGS. 14 (a) and 14(b) show optical micrographs of a composite material formed by using a volumetric ratio of 1:2:2 of FB1 Fiber Cores, (300-500) μm sand, and (2-4) mm sand aggregates, respectively. At higher magnifications, it can be seen that bonding matrix is in the void spaces of sand particles, and a thick layer of bonding matrix has surrounded sand particles to act as a cementing phase also. Table 9 shows certified ASTM property testing by CTL, Illinois and the mechanical properties of the present microstructures in one embodiment. These values should not be viewed as limiting but only as exemplary. For example, additional embodiments my include composite materials with an abrasion resistance having an average wear of less than 1.00 mm using ASTM C 944 instead of having to be exactly 0.38 mm. This composite material has mechanical properties like High Performance Concrete, and in this particular case 20 vol. % of bonding matrix was used to bond the entire structure.

TABLE 9 ASTM certification of a typical Hydrate Free Concrete (HFC4) by CTL (Construction Technology Laboratory, Skokie, Illinois) Hydrate Free FHWA HPC Physical Properties ASTM Concrete Grade⁵ Compressive Strength (psi) C 39 6720 ± 95 Grade 1 Modulus of Elasticity (psi) C 469 4.040 × 10⁶ Grade 1 Split Tensile (psi) C 496  390 ± 10 Not available Chloride Permeability C 1202 1565 ± 56 Grade 1 (Coulombs) Abrasion Resistance C 944 0.38 mm Grade 3 average wear Freeze and Thaw C 666 300 cycles Less than (Number of Cycles) (45-50% strength): Grade 1 DF = 10 Scaling Resistance C 672 x < 1 Grade 3 Shrinkage C 157 Negligible Grade 3 ⁵http://www.fhwa.dotgov/BRIDGE/HPCdef.htm.

Example 3

FIGS. 15(a)-15(b) show the variation of thermal strain of FB1B from −40 to 100° C. during thermal cycling for 2 consecutive cycles. No signs of thermal hysteresis, or phase changes were observed during thermal cycling. Table 10 summarizes thermal properties of P2 and P3 compositions. FIG. 16 shows variation of specific heat from RT to 500° C. of P3 (Table 4). Specific heat increased gradually from 0.711 (J/g²C) to 1.274 (J/g-° C.). No phase change or change in thermal properties of the P3 composition was observed. Clearly, similar types of bonding elements in their pure form, or incorporated into composite composition can be used in high temperature applications like fire resistance etc.

TABLE 10 Summary of thermal properties of P2 and P3 compositions (Table 3) Physical Properties P3 P2 Thermal Conductivity 1.7 (RT) 1.0 (RT) (W/m · k) 1.9 (250° C.) 1.6 (250° C.) Specific Heat (J/g ° C.) 0.7 NA Thermal Expansion (10⁻⁶/° C.) 4.0 NA

By using Table 10, thermal conductivity and thermal expansion of different composite materials by using bonding elements and using a simple rule of mixtures approximation can be calculated. For example, a composite material of 30 vol. % P3 bonding matrix with cork will have a calculated thermal conductivity of 0.55 W/m.K. Similarly, a composite material of 30 vol. % P3 bonding matrix with AlN can have thermal conductivity between 146-196 W/m.k. Moreover, these values can be further regulated by varying the content and porosity of the bonding elements. For example, it is also possible to use 10 vol. % porous P2 matrixes to bind perlite and have thermal conductivity as low as 0.13 W/m.K. In brief, there are numerous combinations and permutations which can be used to tailor thermal properties.

Preliminary results also showed that FB1A samples were able to withstand 10 cycles of thermal shock from 200° C. and then quenching them in water.

Example 4

Properties like blended cements, high strength mortars, and stones like Granite, Sandstone, and Terracotta.

Wollastonite based bonding matrices (Tables 3 and 4) have the appearance of marble or limestone. It can be used as an architectural construction material in a pristine form for decorative purposes. It is also possible to tailor the appearance by adding different colorant additives (Table 11). FIGS. 17(a)-17(c) show typical examples of sandstone, granite, and terracotta mimics prepared by adding colorants in the bonding matrix. CPC composition series (Table 12) was used to prepare different sandstone mimics. Since bonding elements are blended with sand so these composition materials can be used as substitutes for mortar, grouts, or high strength structural bricks also. Similarly, by adding different colors in bonding matrix (Tables 3 and 4) different types of colors and textures can be generated. In such manner, the composite material may be made to exhibit color and texture resembling natural stones described herein. Alternatively, the composite material may be made to exhibit color and texture resembling architectural concrete described herein. Table 13 summarizes physical properties of different stones. Except Quarzite and Granite, compressive strengths of the all the listed solids are less than 69 MPa. Average compressive strength of all the different composite materials of the CPC series is greater than 69 MPa (Table 12). Moreover, average compressive strengths of FB1A and FB1B compositions (bonding matrix without any additives, Table 3 and previous discussion) are between 147-300 MPa. Clearly, physical properties of geomimetic ceramic materials are better than natural stone. By using the concept explained earlier it is also possible to mimic other natural rocks like traventine, serpentine, etc.

TABLE11 Different types of colorants Color Pigment Red Iron oxide (hematite) Yellow Iron Oxide Green Chromium Oxide Blue Cobalt Oxide Black Carbon, Iron oxide (magnetite) Brown Iron Oxide

TABLE 12 Summary of compositions of different blends Masonary Sieved Sieved Wollastonite Sand Sand Sand Compressive Flexural Fiber Core^(‡) (300-500 CaCO₃ (500-800 (800-1400 Strength Strength Composition d₅₀ = 9 μm μm)‡ (<40 μm)^(‡) mm)^(‡) μm)^(‡) (MPa) (MPa) FB1B 100 — — — — 147 ± 24 26 ± 5 BC1 48 — 52 — — — 21 ± 2 CPC1 50 50 — — — 100 ± 11   20 ± 1.5 CPC2 33 67 — — — 87 ± 1 14.4 ± 1.5 CPC3 33 — — 67 — 89 ± 5   22 ± 5.5 CPC4* 50 — — 50 — 103 ± 4  — CPC5 33 — — — 67 68 ± 9 — ^(‡)All compositions are in vol % *Certified by CTL (Skokie, IL)

TABLE 13 Physical properties of different stones Compressive Flexural Strength Strength Absorption Density Stone ASTM (MPa) (MPa) (wt. %) (g/c.c) Traventine C 1527-3 52 6.9 2.5 2.3 Serpentine C 1526-08 69 6.9 0.2 2.56 Marble C 503-08 52 7 0.2 2.6-2.8 Limestone C 568-08 (12-55) 2.9-7 (3-12) 1.76-2.56 Sandstone C 616-08 27.6 2.4 8 2 Quarzite C 616-08 68.9 6.9 3 2.4 Sandstone Quartzite 138 13.9 1 2.56 Granite C 615-03 131 10.34 0.4 2.56

Furthermore, it is also possible to fabricate structures with low water absorption also. For example, CPC2 (Table 12) has a water absorption of 5 wt. %. It is already comparable to sandstone (Table 14). By adding 1 wt. % fumed silica (d₅₀<1 μm) in CPC2 type compositions, the water absorption can be further reduced to 2.6 wt. %.

TABLE 14 Compressive strengths of high strength hydrate free concretes (Certified by CTL) Sieved Sand^(‡) Water 500- Basalt^(‡) Silica Compressive Absorption Wollastonite^(‡) 300-500 800 (6-8 Dolostone^(‡) Aggregates^(‡) Strength ASTM C67 Composition (d₅₀ = 9 μm μm mm) (2-4 mm) (2-4 mm) (MPa)* (wt %) HFC4 20 40 — — 40 47 ± 1 8.3 ± 1.0  HSHFC1 21 — 42 37 — — 80 ± 8 3.1 ± 0.9  HSHFC2 15 — 30 55 — — 65 ± 5 4.7 ± 00.6 HSHFC3 20 — 41 — 39 — 82 ± 7 — ^(‡)All compositions are in vol % *Certified by CTL (Skokie, IL) Density of Basalt = 2.9 g/c.c, density of wollastonite = 2.9 g/c.c, density of dolosone = 2.7 g/c.c, density of sand = 2.6 g/c.c, density of CaCO₃ = 2.7 g/c.c, density of steel = 7.8 g/c.c, density of gravel = 2.6 g/c.c

Comparison of structural concrete with HFC.

Structural concrete has a compressive strength of 35 MPa. By making a composite material of wollastonite core fibers with sand and different types of aggregates, it is possible to attain a wide variety of strengths which are comparable to structural concrete. Table 15 shows few simple compositions of hydrate free concrete (HFC), which showed similar strength to that of structural concrete and therefore suitable in all applications of structural concrete.

TABLE 15 Compressive strength of different compositions of hydrate free concrete Sieved Wollatonite Sand River Silica Com- Fiber (200-500) Gravel Aggregate Compressive position Cores^(‡) μm^(‡) (1/4″)^(‡) (2-4 mm)^(‡) Strength (MPa) HFC1* 1 2 1 — 42 ± 4  HFC2 1 2 2 — 26 HFC3 1 2 4 — 14 HFC4* 1 2 — 2 47 ± 1  HFC5 1 2 — 4 31 ^(‡)All compositions are in vol % *Certified by CTL (Skokie, IL)

The initial composition here is described as the “composite” rather than describing the final composition. The exact final product in terms of chemical and phase composition is unknown. On the other hand, the initial composition can be precisely specified. This is true for all the described examples, not just this one.

Comparison of High Strength and Performance HFC with HSC (High Strength Concrete) and High Performance Concrete (HPC)

As discussed in an earlier example, the HFC4 composite material performs like high performance concrete in mechanical strength (Table 9). In addition, it has also Cl permeability like Grade 1 HPC. Interestingly, HFC4 have high abrasion resistance, scaling resistance and shrinkage like Grade 3 High Performance Concrete. It is interesting to note that even without addition of air entraining mixtures, HFC4 survived 300 freeze-thaw cycles as specified by ASTM C666, however, it's DF (Durability Factor) decreased to 10. Modifications to the sand and aggregate components of the concrete formulations can increase this Durability Factor to 93 after 163 cycles by ASTM C666.

By using advanced processing methods, better packing can be achieved in HFC composite materials (Table 14). For example, water absorption decreased from 8.3 wt % in HFC4 to 3.1 and 4.7 wt % in HSHFC1 and HSHFC2. As expected, compressive strength also increased in these composite materials. HFC4 showed a compressive strength of 47 MPa while the compressive strengths of HSHFC1 and HSHFC2 increased to 80 MPa and 65 MPa, respectively.

Early Strength Cement or Concrete

FIG. 18 shows variation of reaction time on mechanical strength. After a reaction time of 5 h, a compressive strength of 60 MPa is reached. These systems can be used to prepare early strength cementing phase, or as concretes in composite systems. Portland cement concrete does not do this in such short a time.

Comparison of Engineered HFC Compositions with UHPC (Ultra High Performance Concrete)

FIGS. 19(a)-19(c) show typical ductile failure of FB1B bonding matrix reinforced with 10 wt. % DRAMIX steel fibers (ZP305, Bekaert Corporation, Marietta, Ga.). DRAMIX is a proprietary cold drawn low C steel fiber having length≈30 mm and diameter≈0.5 mm with hooked ends glued together. However, it is expected that similar results may be achieved with various other steel fibers.

CPC2 type composition (Table 12) was also infiltrated with 10 wt. % (4 vol. %) steel fibers (FRCPC2, Table 16). These compositions showed nearly 1.4 times higher flexural strength than the CPC composition and simultaneously ductile failure also (FIG. 19(b)). Similarly, when CPC2 was infiltrated with 2.5 wt. % PVA fibers (RFS400, NYCON PVA, 18 mm fibers, Fairless Hills, Pa.), then they failed at a lower strength, but showed enhanced strength retention.

TABLE 16 Summary of different compositions fabricated by modifying CPC2 Wollastonite^(‡) Steel Wire Fibers^(‡) Masonary (NYCOR (Dramix) Flexural Wollastonite^(‡) Sand^(‡) 100) As Strength Composition d₅₀ = 9 μm (300-500) μm d₅₀ = 800 μm received Rusted (MPa) CPC2 33 67 — — — 14.4 ± 1.5 SRCPC2 22 46 31 — — 16.2 ± 1.3 FRCPC2 32 64 — 4 — 20.0 ± 3.5 RFRCPC2 32 64 — — 4 18.1 ± 2.9 All compositions are in vol %

In order to tailor and enhance the interaction of bonding elements with steel, these fibers were allowed to oxidize in air (rust formation). Subsequently, 10 wt. % (4 vol. %) rusted fibers were also put in CPC2 matrix (RFRCPC2, Table 16). Due to enhanced debonding at the interface, these new compositions showed enhanced ductility (region II in FIG. 19(c)). FIGS. 20(a)-20(f) show the steel-bonding matrix interface. Clearly, during the curing reaction the original interface has interacted with the steel surface. These composite materials are referred to as “hydrothermally controlled interfacial engineered ductile composites”.

It is believed that the interface of the steel fiber may have a unique composition and structure.

Table 17 shows comparison of properties of Ductal® (A propriety ultra high performance concrete developed by Lafarge (US/Canada Region, Calgary, Alberta, Canada, T2W 4Y1) with FB1B (a wollastonite core fiber based bonding matrix, Table 2B). FB1B has higher compressive and flexural strength as compared to Ductal®-FO (without thermal treatment), but slightly lower compressive and flexural strength as compared to Ductal®-FM or Ductal®-AF (Ductal®-FM with thermal treatment). The thermal expansion of FB1B is higher than all the different varieties of Ductal®. FB1B has brittle failure. By using steel fibers and further engineering of particles and fibers, it is possible to fabricate composite materials with ultra high performance. These materials can be potentially used in all applications of ultra high performance concrete materials, which will be discussed in the following section.

TABLE 17 Comparison of properties of wollastonite core fiber based bonding matrix with Ductal ® (A type of Ultra high performance concrete) Coefficient Com- of Flexural pressive Elastic Thermal Strength Strength Modulus Expansion Material (MPa) (MPa) (GPa) (/° C.) Ductal ®-FM or 30-40 150-180 50 11.8 × 10⁻⁶ Ductal ®-AF With Thermal Treatment (FM is metal fibers) Ductal ®-FO 15-20 100-140 45 11.8 × 10⁻⁶ Without Thermal Treatment (FO - Organic Fibers) Wollastonite 26 ± 5  147 ± 24  32  7.4 × 10⁻⁶ core fiber based (−40° C. − 100° C.) bonding matrix (FB1B - Table 4) Wollastonite 25-30 NA NA NA core fiber based bonding matrix (FB1B - Table 4) with 10 wt. % fibers CPC2 with 10 wt. % 18-25 NA NA NA metal fibers (FRCPC2)

Novel Ductile and Impact Resistant Structures

Table 18 summarizes different composite materials fabricated by using longer wollastonite fiber cores (d₅₀=800 μm). FIG. 21 shows a typical microstructure of SRC3 composite materials (Table 18). As the concentration of longer fibers are increased in these self reinforced structures, flexural strength decreases, however, as summarized in Table 20 impact resistance improves further. For example, pristine FB1B bonding matrix fails at 0.75 ft.lb impact, whereas, when they are self-reinforced with longer fiber cores, they fail at 4.5 ft.lb impact. Traditional monolithic materials like Granite, Travertine, Marble fail at 1.2 ft.lb, whereas, Metro-Dade approved Pittsburgh Corning Thickset 90 (Pittsburgh Corning Corporation, Pittsburgh, Pa.) fails at 2.2 ft.lb impact. It is clear that SRCC has one of the highest impact resistances among different types of construction materials.

TABLE 18 Summary of compositions of self reinforced composites Wollastonite ‡ Wollastonite‡ Wollastonite‡ Flexural Com- (NYAD 400) (NYAD M200) (NYCOR 100) Strength position d₅₀ = 9 μm d₅₀ = 15 μm d₅₀ = 800 μm (MPa) FB1B 100 — — 26 ± 5  SRC1  80 — 20 ≈23   SRC2  50 — 50 ≈18.5 SRC3  14 29 57 17.5 ± 0.5  ‡All compositions are in vol %

Super-Blends

In earlier examples, concepts of “Self Reinforced Cementitous Composites (SRCC)” and Hydrothermally Controlled Interfacially Engineered Ductile Composites” were explained. It is possible to integrate these two approaches and fabricate a new class of materials called Super-blends (Table 19). FIG. 22 shows ductile behavior of FSRBC1 composite material. Four main regions were observed during deformation: (I) Elastic, (II) Plastic, (III) Strength retention, and (IV) Gradual failure. FIG. 22 shows bending of this composite material during 3-point bending. These solids have high impact resistance (Table 20). For example, FSRBC1 has an impact resistance of 13 ft.lb, which is about 6 times higher than that for Pittsburgh-Corning Thickset 90.

TABLE 19 Different compositions used for fabricating super blends Wollastonite Dolomite^(‡) Wollastonite^(‡) Steel Wire Flexural Fiber Core^(‡) CaCO₃ ^(‡) (Dolocron (NYCOR 100) Fibers^(‡) Strength Composition d₅₀ = 9 μm (<30 μm) 4213) (d₅₀ = 800 μm (Dramix) (MPa) BC1 38 62 — — — 21 ± 2 SRBC1 32 52 — ′16  — 14 ± 4 FSRBC1 37 40 — 19 4 22 ± 4 DC1 34 — 66 — —  9.7 ± 1.6 SRDC1 40 — 40 20 — 18.7 ± 1.7 FSRDC1 38 — 39 19 4 20.9 ± 2.7 ^(‡)All compositions are in vol %

TABLE 20 Impact resistance of different compositions by using ball impact (Certified by Trinity/ERD, Columbia, SC) FPS Units m v KE p h Material Systems (lbs) (ft/s) (ft. lb) (lb. ft/s) (ft) FSRBC1, FRCPC2* 2.3 19 13 44 6 SRC3 (F) 1.2 15.5 4.5 18.6 3.2 SRC3 (P) 0.75 20.4 4.9 15.3 6.5 Pittsburgh Corning 1.2 11.0 2.2 13.1 1.6 Thickset 90 (F) SRC 1 (F) 0.75 15.5 2.8 11.6 3.25 Pittsburgh Corning Thickset 1.2 8 1.2 9.6 1 90 (P), Marble (F), Traventine (F), Granite (F) SRC1 (P) 0.75 10.9 1.4 8.2 1.6 FB1B (F) 0.75 8.0 0.75 6.0 1 FB1B (P) 0.75 5.7 0.4 4.3 0.5 FB 1B (P) 0.75 4.0 0.2 3.0 0.25 *Internal testing F — Fail, P — Pass

These types of solids can be used for applications requiring properties of blast and impact resistant, ultra high performance and high performance concrete like properties, damage resistant applications like high freeze-thaw, adverse environment applications. Moreover, it is further possible to substitute the blend with different types of additives according to specialized applications like sulfate resistance, chloride resistance etc., but not limited to these. Table 19 shows an example where dolomite fillers can be used also instead of CaCO₃ or sand.

Example 5

Novel Chemistries of Bonding Elements

Similarly, it is also possible to design a wide range of structures by using chemistries different from wollastonite above but have the common ability to use the disproportionation reaction to form the novel bonding element described in this invention. For example, FIGS. 23(a)-23(e) and FIGS. 24(a)-24(d)_show microstructures of bonding matrices derived from olivine (Mg₂SiO₄) and diopside (MgCaSi₂O₆) precursors. These bonding matrices have a compressive strength of 162±15 MPa and −93 MPa, respectively. For example, Olivine is composed of unreacted Mg₂SiO₄ core surrounded by unreacted silica layers (depleted zone) and MgCO₃ crystals acting as a cementing phase to bind the entire structure (FIG. 23(c)). These unreacted cores can have different morphologies, for example, FIG. 23(d) shows how MgCO₃ crystals precipitated inside cup-shaped Olivine grains.

FIGS. 24(a)-24(d) show microstructures of diopside grains as cores. These grains are surrounded by amorphous silica, and dolomite (CaCO₃.MgCO₃) and/or magnesite (MgCO₃) and/or CaCO₃ particles. As with wollastonite, these materials can be used to make novel microstructures via the various methods described earlier. Furthermore, as mentioned earlier, there is a huge number of ceramics that can undergo this disproportionation reaction, which are both minerals and waste products.

It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the invention. Thus, it is intended that the present invention cover the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents. 

What is claimed is:
 1. A bonding matrix comprising a plurality of bonding elements, each bonding element comprising: a core, wherein the core has a first chemical composition that includes one or more chemical elements; a silica-rich first layer at least partially covering a peripheral portion of the core; and a calcium carbonate and/or magnesium carbonate-rich second layer at least partially covering a peripheral portion of the first layer, wherein the bonding matrix is prepared from a porous solid body, the porous solid body comprises a plurality of precursor particles, the precursor particles have a mean particle size of less than 70 μm, and the precursor particles are transformed into the bonding elements, wherein the core comprises at least one synthetic formulation having chemical elements M, Me, and O (oxygen) and/or OH group, M is an alkaline earth metal selected from calcium or magnesium, and Me comprises silicon.
 2. The bonding matrix of claim 1, wherein the first chemical composition includes at least two different chemical elements, wherein cations associated with the silica-rich first layer correspond to a first one of the at least two different chemical elements of the first chemical composition, and wherein cations associated with the calcium carbonate and/or magnesium carbonate-rich second layer correspond to a second one of the at least two different chemical elements of the first chemical composition.
 3. The bonding matrix of claim 1, wherein the first chemical composition includes at least two different chemical elements, wherein cations associated with the silica-rich first layer correspond to a first one of the at least two different chemical elements of the first chemical composition, and wherein cations associated with the calcium carbonate and/or magnesium carbonate-rich second layer correspond to the first one of the at least two different chemical elements of the first chemical composition.
 4. The bonding matrix of claim 1, wherein the first chemical composition includes only one chemical element.
 5. The bonding matrix of claim 1, wherein cations associated with the silica-rich first layer are bonded with anions corresponding to one of the chemical elements of the first chemical composition.
 6. The bonding matrix of claim 5, wherein cations associated with the calcium carbonate and/or magnesium carbonate-rich second layer are bonded with anions corresponding to a reactant.
 7. The bonding matrix of claim 1, wherein cations associated with the silica-rich first layer are bonded with anions corresponding to a first reactant.
 8. The bonding matrix of claim 7, wherein cations associated with the calcium carbonate and/or magnesium carbonate-rich second layer are bonded with anions corresponding to a second reactant.
 9. The bonding matrix of claim 1, wherein the core is equiaxed.
 10. The bonding matrix of claim 1, wherein the core is elliptically-shaped.
 11. The bonding matrix of claim 1, wherein the core is fiber-shaped.
 12. The bonding matrix of claim 1, wherein the first layer is an amorphous layer.
 13. The bonding matrix of claim 1, wherein the core has a symmetrical shape.
 14. The bonding matrix of claim 1, wherein the core has a non-symmetrical shape.
 15. The bonding matrix of claim 1, wherein the core is in the shape of a flake.
 16. The bonding matrix of claim 1, wherein the core comprises CaSiO₃.
 17. The bonding matrix of claim 1, wherein the core comprises MgSiO₃.
 18. The bonding matrix of claim 1, wherein the first layer is a crystalline layer.
 19. The bonding matrix of claim 1, wherein the first layer comprises an oxide or a hydroxide of silicon.
 20. The bonding matrix of claim 1, wherein the first layer comprises silicon oxide.
 21. The bonding matrix of claim 1, wherein the first layer comprises silicon hydroxide.
 22. The bonding matrix of claim 1, wherein the second layer is composed of the carbonate bonds with one or more active particulates selected from the group consisting of limestone, marble dusts, calcium carbonate rich aggregates, gypsum, sand, silica rich aggregates, and combinations thereof.
 23. The bonding matrix of claim 1, wherein the second layer is a continuous phase or discontinuous phase.
 24. The bonding matrix of claim 1, wherein the bonding matrix is porous.
 25. The bonding matrix of claim 1, wherein the bonding elements are oriented in the 1-D orientation, 2-D orientation, 3-D orientation, randomly oriented, or form a percolation network.
 26. The bonding matrix of claim 1, wherein at least some of the bonding elements are in contact with one another.
 27. The bonding matrix of claim 1, wherein the second layer is composed of CaCO₃ which bonds with one or more active particulates selected from the group consisting of limestone, marble dusts, calcium carbonate rich aggregates, gypsum, sand, silica rich aggregates, and combination thereof.
 28. The bonding matrix of claim 1, further comprising a hydrate-free cementitious bond.
 29. A composite material comprising: the bonding matrix according to claim 1; and a filler material incorporated in the bonding matrix.
 30. The composite material of claim 29, wherein the filler material includes an inert material.
 31. The composite material of claim 30, wherein the inert material comprises a plurality of equiaxed particles.
 32. The composite material of claim 30, wherein the inert material comprises a plurality of anisotropic particles.
 33. The composite material of claim 30, wherein the inert material comprises a combination of equiaxed particles and anisotropic particles.
 34. The composite material of claim 29, wherein the filler material includes an active material.
 35. The composite material of claim 34, wherein the active material comprises a plurality of equiaxed particles.
 36. The composite material of claim 34, wherein the active material comprises a plurality of anisotropic particles.
 37. The composite material of claim 34, wherein the active material comprises a combination of equiaxed particles and anisotropic particles.
 38. The composite material of claim 29, wherein the filler material comprises: a first plurality of first size particles and a second plurality of second size particles, the second size particles being substantially larger in size than the first sized particles, and wherein the bonding matrix, the first size particles and the second size particles are arranged such that the composite material forms a hierarchic structure.
 39. The composite material of claim 38, wherein the bonding matrix is substantially arranged in porous spaces between adjacent first size particles, and wherein the adjacent first size particles are arranged in porous spaces between adjacent second size particles.
 40. The composite material of claim 39, wherein the bonding matrix at least partially covers a peripheral portion of each of the adjacent first size particles.
 41. The composite material of claim 29, wherein the bonding elements are aligned in a 1-D orientation.
 42. The composite material of claim 29, wherein the bonding elements are aligned in a 2-D orientation.
 43. The composite material of claim 29, wherein the bonding elements are aligned in a 3-D orientation.
 44. The composite material of claim 29, wherein the bonding elements are arranged in a random orientation.
 45. The composite material of claim 29, wherein the composite material has a Vicker's hardness between about 1 GPa and 30 GPa.
 46. The composite material of claim 29, wherein the composite material has a compressive strength varying between 14 to about 3,000 MPa and a flexural strength of less than about 380 MPa.
 47. The composite material of claim 29, wherein the composite material exhibits creep strain of less than 60×10⁻⁶/psi.
 48. The composite material of claim 29, wherein the composite material exhibits Cl— permeability of less than 700 C.
 49. The composite material of claim 29, wherein the composite material is self reinforced and has a ball impact resistance greater than 6 J.
 50. The composite material of claim 29, wherein the composite material is reinforced with steel fibers and has a ball impact resistance greater than 10 J.
 51. The composite material of claim 29, wherein the composite material exhibits ductile behavior and strength retention during failure.
 52. The composite material of claim 29, wherein the composite material has a thermal shock resistance.
 53. The composite material of claim 29, wherein the composite material has a thermal conductivity of greater than about 0.13 W/m.k, and less than about 196 W/m.k.
 54. The composite material of claim 29, wherein, the composite material exhibits at least one of the following properties: (i) modulus of elasticity of at least 4.04×10⁶ psi; (ii) split tensile strength of at least 390 psi; (iii) average wear of less than 1.00 mm using ASTM C 944; (iv) freeze-thaw resistance of at least 300 cycles by ASTM C666; (v) visible scaling resistance of x<1 when testing using ASTM C672; (vi) negligible shrinkage measured by ASTM C157; and (vii) negligible alkali-silicate reaction.
 55. The composite material of claim 29, wherein the composite material has a thermal expansion coefficient between 3×10⁻⁶/C and 15×10⁻⁶/° C.
 56. The composite material of claim 29, wherein the composite material has a heat capacity between 6 and 900 J/mole.K.
 57. The composite material of claim 29, wherein the composite material has a reflectivity coefficient between 0.04 and 0.9.
 58. The composite material of claim 29, further comprising a porosity of about 1 to about 99 vol. %.
 59. The composite material of claim 58, wherein the porosity is about 1 to about 70 vol. %.
 60. The composite material of claim 59, wherein the porosity is about 1 to about 10 vol. %.
 61. The composite material of claim 59, wherein the porosity is about 50 to about 70 vol. %.
 62. The composite material of claim 29, wherein the bonding matrix comprises a volume fraction of about 1 to 99 vol. %.
 63. The composite material of claim 62, wherein the volume fraction is about 8 to 99 vol. %.
 64. The composite material of claim 63, wherein the volume fraction is about 8 to 30 vol. %.
 65. The composite material of claim 29, wherein the bonding matrix shows at least one interconnectivity pattern.
 66. The composite material of claim 29, further comprising a hierarchic structure comprising at least one of 1-level, 2-level, 3-level, 4-level, or combination thereof.
 67. The composite material of claim 29, further comprising a hydrate-free cementitious bond.
 68. The composite material of claim 29, further comprising at least one additive comprising calcium carbonate, gypsum, sand, aggregates, minerals, metallic fibers, organic fibers, ceramic fibers, waste cork granules, defoamers, ultrafine particles, low density aggregates, high density aggregates, or combination thereof.
 69. The composite material of claim 29, further comprising a monolithic solid.
 70. The composite material of claim 29, further comprising at least one of a polymer, a coloring agent, a dispersant, a metal or combination thereof.
 71. The composite material of claim 29, further comprising a color and texture resembling natural stones.
 72. The composite material of claim 29, further comprising a color and texture resembling a material selected from the group consisting of marble, limestone, sandstone, granite, terracotta, travertine rock, and serpentine rock.
 73. The composite material of claim 29, further comprising a color and texture resembling architectural concrete.
 74. The composite material of claim 29, further comprising a color and texture resembling one selected from the group consisting of mortar, grouts, and high strength structural brick. 